LNP Thermocomp® UC-1006 Polyphthalamide, Carbon Fiber Reinforcement  (discontinued **)

Category Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), Carbon Fiber Filled
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LNP Thermocomp® UC-1006 Polyphthalamide, Carbon Fiber Reinforcement  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Forms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are still active under new names instituted after the SABIC purchase.
Physical Properties Metric English Comments
Specific Gravity 1.32 g/cc
1.32 g/cc
Method A; ASTM D792
Water Absorption 0.30 %
0.30 %
at 24 hrs; ASTM D570
Linear Mold Shrinkage 0.0020 cm/cm
0.0020 in/in
ASTM D955
Linear Mold Shrinkage, Transverse 0.0060 cm/cm
0.0060 in/in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 287 MPa
41600 psi
ASTM D638
Tensile Strength, Yield 287 MPa
41600 psi
ASTM D638
Elongation at Break 1.5 %
1.5 %
ASTM D638
Elongation at Yield 1.5 %
1.5 %
ASTM D638
Tensile Modulus 26.1 GPa
3790 ksi
ASTM D638
Flexural Strength 414 MPa
60000 psi
ASTM D790
Flexural Modulus 22.6 GPa
3280 ksi
ASTM D790
Izod Impact, Notched 0.747 J/cm

@Thickness 3.18 mm
1.40 ft-lb/in

@Thickness 0.125 in
ASTM D256
Izod Impact, Unnotched 8.27 J/cm

@Thickness 3.18 mm
15.5 ft-lb/in

@Thickness 0.125 in
ASTM D256
Izod Impact, Notched (ISO) 6.40 kJ/m²
3.05 ft-lb/in²
ISO 180
Izod Impact, Unnotched (ISO) 51.7 kJ/m²
24.6 ft-lb/in²
ISO 180
Falling Dart Impact 8.91 J
6.57 ft-lb
ASTM D3763
Impact Test 2.30 J
1.70 ft-lb
Multi-Axial Instrumented Impact Energy; ISO 6603-2
Coefficient of Friction, Dynamic 0.27
0.27
vs. Steel - @ 40 psi, 50 ft/min, tested in accordance with LNP WI-0687; ASTM D1894
Coefficient of Friction, Static 0.21
0.21
vs. Steel @ 40 psi, tested in accordance with LNP WI-0687; ASTM D1894
K (wear) Factor 12.1 x 10-8 mm³/N-M
6.00 x 10-10 in³-min/ft-lb-hr
40psi, 50ft/min; tested in accordance with LNP WI-0687
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 286 °C
547 °F
Unannealed; ASTM D648
Processing Properties Metric English Comments
Melt Temperature 316 - 329 °C
601 - 624 °F
Mold Temperature 135 - 163 °C
275 - 325 °F
Drying Temperature 121 - 149 °C
250 - 300 °F
Dry Time 4 hour
4 hour
Moisture Content 0.15 %
0.15 %
Suggested
Back Pressure 0.172 - 0.345 MPa
24.9 - 50.0 psi