LG Chemical Lupox® SV1120M PBT
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | LG Chemical |
| Trade Name | Lupox® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical Lupox® SV1120M PBT.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Injection Molding, PBT, General Purpose, High ViscosityApplication: Films & Sheets, Optical Loose TubeCAS No. 65997-17-3 and 24968-12-5Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.31 g/cc | 1.31 g/cc | ASTM D792 |
| Water Absorption | 0.080 % @Temperature 23.0 °C, Time 86400 sec |
0.080 % @Temperature 73.4 °F, Time 24.0 hour |
ASTM D570 |
| Maximum Moisture Content | 0.020 | 0.020 | Injection Molding |
| Linear Mold Shrinkage, Flow | 0.018 - 0.021 cm/cm @Thickness 3.20 mm |
0.018 - 0.021 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 10 g/10 min @Load 2.16 kg, Temperature 260 °C |
10 g/10 min @Load 4.76 lb, Temperature 500 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 47.1 MPa @Thickness 3.20 mm |
6830 psi @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Elongation at Break | >= 200 % @Thickness 3.20 mm |
>= 200 % @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Flexural Yield Strength | 83.4 MPa @Thickness 3.20 mm |
12100 psi @Thickness 0.126 in |
2.8mm/min; ASTM D790 |
| Flexural Modulus | 2.45 GPa @Thickness 3.20 mm |
356 ksi @Thickness 0.126 in |
2.8mm/min; ASTM D790 |
| Izod Impact, Notched | 0.392 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
0.735 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 225 °C | 437 °F | @ Break; ASTM D3418 |
| Deflection Temperature at 0.46 MPa (66 psi) | 154 °C @Thickness 6.40 mm |
309 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 57.0 °C @Thickness 6.40 mm |
135 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 230 - 240 °C | 446 - 464 °F | Injection Molding |
| Middle Barrel Temperature | 240 - 250 °C | 464 - 482 °F | Injection Molding |
| Front Barrel Temperature | 250 - 260 °C | 482 - 500 °F | Injection Molding |
| Nozzle Temperature | 250 - 260 °C | 482 - 500 °F | Injection Molding |
| Mold Temperature | 40.0 - 80.0 °C | 104 - 176 °F | Injection Molding |
| Drying Temperature | 100 - 120 °C | 212 - 248 °F | Injection Molding |
| Dry Time | 3.00 - 5.00 hour | 3.00 - 5.00 hour | Injection Molding |
Users viewing this material also viewed the following:
- Network Polymers NPP 25-2102
- Lehmann & Voss LUVOCOM® 1-0867 Polyamide 66, with aramid reinforcement and PTFE, lubricant modified, heat stabilized
- Unifrax Excelfrax® 1800 Board Microporous Insulation
- Trelleborg Emerson & Cuming Eccobond® 51 Two-Component General Purpose Epoxy Adhesive
- Asahi Kasei Thermylene® P6-10FG-0570 10% Glass Fiber Reinforced, Flame Retardant
- Beijing Ranger Chem PBT-201-G25 Flame Retarding FR PBT
- H.C. Starck Amperit® 415.1 CoNiCrAlY (MCrAlY)
- Kennametal Stellite Stellite® 31 PM after P/M processing, aged 8 hours at 802°C air cooled