- LG Chemical LUPOY GP-5000FQ General Purpose PC/ABS Alloy, Unreinforced, Excellent Flow
LG Chemical LUPOY GP-5000FQ General Purpose PC/ABS Alloy, Unreinforced, Excellent Flow
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | LG Chemical |
| Trade Name | LUPOY |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical LUPOY GP-5000FQ General Purpose PC/ABS Alloy, Unreinforced, Excellent Flow.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Among the characteristics of LUPOY polycarbonate resins are excellent mechanical properties, high heat resistance, high impact strength, and dimensional stability.Applications:Automotive: Automotive front ends, cluster pad main panel (instrument panel), lower cluster pad main, console box, glove box cover, door, wheel cover and cap, defroster grill, back mirror housingElectrical and Electronic: Monitor housing, fax housing, notebook PC housing, cellular phone case, fax and copy machine frame, CD ROM drive tray and main frame, relay case, connector, switchIndustrial Parts and Household Appliance: Helmet, terminal box, electrical tool housing, industrial bobbin, distributing board box, power tool component, gears and cams, water meter housingInformation Provided by LG Chem
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.17 g/cc | 1.17 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0060 cm/cm | 0.0060 in/in | ASTM D955 |
| Melt Flow | 14 g/10 min @Load 2.16 kg, Temperature 250 °C |
14 g/10 min @Load 4.76 lb, Temperature 482 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 114 | 114 | ASTM D785 |
| Tensile Strength, Yield | 56.0 MPa | 8120 psi | ASTM D638 |
| Elongation at Break | 25 % | 25 % | ASTM D638 |
| Flexural Strength | 82.0 MPa | 11900 psi | ASTM D790 |
| Flexural Modulus | 2.40 GPa | 348 ksi | ASTM D790 |
| Izod Impact, Notched | 2.95 J/cm @Temperature 23.0 °C |
5.53 ft-lb/in @Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 92.0 °C | 198 °F | ASTM D648 |
| Flammability, UL94 | V-2 @Thickness 1.50 mm |
V-2 @Thickness 0.0591 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 230 - 270 °C | 446 - 518 °F | |
| Middle Barrel Temperature | 240 - 280 °C | 464 - 536 °F | |
| Front Barrel Temperature | 250 - 290 °C | 482 - 554 °F | |
| Nozzle Temperature | 250 - 290 °C | 482 - 554 °F | |
| Melt Temperature | 260 - 300 °C | 500 - 572 °F | |
| Mold Temperature | 70.0 - 110 °C | 158 - 230 °F | |
| Drying Temperature | 70.0 - 100 °C | 158 - 212 °F | |
| Dry Time | 3 - 5 hour | 3 - 5 hour | |
| Screw Speed | 40 - 70 rpm | 40 - 70 rpm |
Users viewing this material also viewed the following:
- Radici Radilon® A RV200 (cond.) Nylon 66
- Covestro Texin® DP7-1157 Thermoplastic Polyurethane + ABS Blend (discontinued **)
- Michelman® DigiPrime® 3000 Primer
- Teijin Panlite® GN-3430R Improved Mold Release, Glass Fiber Reinforced, Flame Resistant Polycarbonate Resin
- Borealis Bormed™ HD850MO Polypropylene Copolymer for Healthcare Applications
- Dow Corning HV 490 EMULSION
- Covestro Bayblend® FR3200 TV PC/ABS Blend
- DSM Akulon® K225-KS Nylon 6 (European and Asian Grade) (Cond)
- Axiall 37740 Wire & Cable Flexible PVC
- Bhansali Engineering Abstron KU600N ABS Heat Resistant
Copyright © lookpolymers.com All Rights Reserved