Category | Polymer , Thermoplastic , Polycarbonate (PC) |
Manufacturer | LATI |
Trade Name | Latilon |
Port | Ningbo port,China |
Trade Terms | FOB, CFR, CIF |
Payment Terms | L/C, T/T, Western Union |
Download PDF | LATI Latilon 28D PC.pdf ![]() |
Price | EMAIL US sales@lookpolymers.com |
Physical Properties | Metric | English | Comments |
---|---|---|---|
Density | 1.20 g/cc | 0.0434 lb/in³ | |
Linear Mold Shrinkage, Flow | 0.0070 - 0.0090 cm/cm | 0.0070 - 0.0090 in/in | |
Linear Mold Shrinkage, Transverse | 0.0070 - 0.0090 cm/cm | 0.0070 - 0.0090 in/in |
Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Elongation at Break | >= 100 % @Temperature 23.0 °C |
>= 100 % @Temperature 73.4 °F |
|
>= 100 % @Temperature 60.0 °C |
>= 100 % @Temperature 140 °F |
||
>= 100 % @Temperature 90.0 °C |
>= 100 % @Temperature 194 °F |
||
>= 100 % @Temperature 120 °C |
>= 100 % @Temperature 248 °F |
||
Elongation at Yield | 2.5 % @Temperature 120 °C |
2.5 % @Temperature 248 °F |
|
3.5 % @Temperature 90.0 °C |
3.5 % @Temperature 194 °F |
||
4.5 % @Temperature 60.0 °C |
4.5 % @Temperature 140 °F |
||
6.0 % @Temperature 23.0 °C |
6.0 % @Temperature 73.4 °F |
||
Tensile Modulus | 1.60 GPa @Temperature 120 °C |
232 ksi @Temperature 248 °F |
|
1.80 GPa @Temperature 90.0 °C |
261 ksi @Temperature 194 °F |
||
2.10 GPa @Temperature 60.0 °C |
305 ksi @Temperature 140 °F |
||
2.40 GPa @Temperature 23.0 °C |
348 ksi @Temperature 73.4 °F |
||
Charpy Impact Unnotched | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
|
NB @Temperature -20.0 °C |
NB @Temperature -4.00 °F |
||
Charpy Impact, Notched | 0.800 J/cm² @Temperature -20.0 °C |
3.81 ft-lb/in² @Temperature -4.00 °F |
|
1.00 J/cm² @Temperature 23.0 °C |
4.76 ft-lb/in² @Temperature 73.4 °F |
Thermal Properties | Metric | English | Comments |
---|---|---|---|
Maximum Service Temperature, Air | 120 °C | 248 °F | |
Deflection Temperature at 0.46 MPa (66 psi) | 125 °C | 257 °F | |
Deflection Temperature at 1.8 MPa (264 psi) | 120 °C | 248 °F | |
Vicat Softening Point | 135 °C @Load 5.00 kg |
275 °F @Load 11.0 lb |
|
Oxygen Index | 26 % | 26 % |
Processing Properties | Metric | English | Comments |
---|---|---|---|
Melt Temperature | 270 - 290 °C | 518 - 554 °F | |
Mold Temperature | 100 - 120 °C | 212 - 248 °F | |
Drying Temperature | 120 - 130 °C @Time 10800 sec |
248 - 266 °F @Time 3.00 hour |
Descriptive Properties | Value | Comments |
---|---|---|
ISO Shrinkage - Pressure | 60 MPa |