LATI Latigloss 57 G/50 F2 PPA, 50% Glass Fiber Reinforced

Category Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), 50% Glass Fiber Reinforced
Manufacturer LATI
Trade Name Latigloss
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Latigloss 57 G/50 F2 PPA, 50% Glass Fiber Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product with high mechanical properties and exceptional surface finish based on Semi-aromatic polyamide (PPA). Glass fibers. Potentially suitable for food/medical contact application. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.63 g/cc
0.0589 lb/in³
Linear Mold Shrinkage, Flow 0.0015 - 0.0030 cm/cm
0.0015 - 0.0030 in/in
Linear Mold Shrinkage, Transverse 0.0030 - 0.0050 cm/cm
0.0030 - 0.0050 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 70.0 MPa

@Temperature 150 °C
 10200 psi

@Temperature 302 °F
130 MPa

@Temperature 120 °C
 18900 psi

@Temperature 248 °F
190 MPa

@Temperature 90.0 °C
 27600 psi

@Temperature 194 °F
225 MPa

@Temperature 60.0 °C
 32600 psi

@Temperature 140 °F
240 MPa

@Temperature 23.0 °C
 34800 psi

@Temperature 73.4 °F
Elongation at Break 1.8 %

@Temperature 23.0 °C
 1.8 %

@Temperature 73.4 °F
2.0 %

@Temperature 60.0 °C
 2.0 %

@Temperature 140 °F
2.1 %

@Temperature 90.0 °C
 2.1 %

@Temperature 194 °F
3.5 %

@Temperature 120 °C
 3.5 %

@Temperature 248 °F
6.0 %

@Temperature 150 °C
 6.0 %

@Temperature 302 °F
Tensile Modulus 5.50 GPa

@Temperature 150 °C
 798 ksi

@Temperature 302 °F
11.0 GPa

@Temperature 120 °C
 1600 ksi

@Temperature 248 °F
14.0 GPa

@Temperature 90.0 °C
 2030 ksi

@Temperature 194 °F
15.5 GPa

@Temperature 60.0 °C
 2250 ksi

@Temperature 140 °F
18.0 GPa

@Temperature 23.0 °C
 2610 ksi

@Temperature 73.4 °F
Charpy Impact Unnotched 7.00 J/cm²
33.3 ft-lb/in²
Charpy Impact, Notched 0.900 J/cm²
4.28 ft-lb/in²
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 150 °C
302 °F
Deflection Temperature at 0.46 MPa (66 psi) 285 °C
545 °F
Deflection Temperature at 1.8 MPa (264 psi) 260 °C
500 °F
Vicat Softening Point 260 °C

@Load 5.00 kg
 500 °F

@Load 11.0 lb
Processing Properties Metric English Comments
Melt Temperature 310 - 340 °C
590 - 644 °F
Mold Temperature 150 - 170 °C
302 - 338 °F
Drying Temperature 120 - 130 °C

@Time 10800 sec
 248 - 266 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa