LATI Larpeek 10 G/60 PEEK, 60% Glass Fiber Reinforced

Category Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) , Polyetheretherketone, PEEK, Glass Fiber Filled
Manufacturer LATI
Trade Name Larpeek
Port Ningbo port,China
Trade Terms EXW, FOB, CFR, CIF
Payment Terms L/C, T/T, PayPal
Download PDF LATI Larpeek 10 G/60 PEEK, 60% Glass Fiber Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Polyetheretherketone (PEEK) based compound. Glass fibers. Very good chemical resistance. Very good thermal properties. Low smoke density and low toxicity index.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.82 g/cc
0.0658 lb/in³
Linear Mold Shrinkage, Flow 0.0015 - 0.0035 cm/cm
0.0015 - 0.0035 in/in
Linear Mold Shrinkage, Transverse 0.0030 - 0.0055 cm/cm
0.0030 - 0.0055 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 160 MPa
<br>@Temperature 150 °C
 23200 psi
<br>@Temperature 302 °F
180 MPa
<br>@Temperature 120 °C
 26100 psi
<br>@Temperature 248 °F
200 MPa
<br>@Temperature 90.0 °C
 29000 psi
<br>@Temperature 194 °F
215 MPa
<br>@Temperature 60.0 °C
 31200 psi
<br>@Temperature 140 °F
225 MPa
<br>@Temperature 23.0 °C
 32600 psi
<br>@Temperature 73.4 °F
Elongation at Break 1.7 %
<br>@Temperature 23.0 °C
 1.7 %
<br>@Temperature 73.4 °F
1.7 %
<br>@Temperature 60.0 °C
 1.7 %
<br>@Temperature 140 °F
1.7 %
<br>@Temperature 90.0 °C
 1.7 %
<br>@Temperature 194 °F
1.7 %
<br>@Temperature 120 °C
 1.7 %
<br>@Temperature 248 °F
1.8 %
<br>@Temperature 150 °C
 1.8 %
<br>@Temperature 302 °F
Tensile Modulus 21.4 GPa
<br>@Temperature 150 °C
 3100 ksi
<br>@Temperature 302 °F
22.0 GPa
<br>@Temperature 120 °C
 3190 ksi
<br>@Temperature 248 °F
22.4 GPa
<br>@Temperature 90.0 °C
 3250 ksi
<br>@Temperature 194 °F
22.7 GPa
<br>@Temperature 60.0 °C
 3290 ksi
<br>@Temperature 140 °F
23.0 GPa
<br>@Temperature 23.0 °C
 3340 ksi
<br>@Temperature 73.4 °F
Charpy Impact Unnotched 5.00 J/cm²
23.8 ft-lb/in²
Charpy Impact, Notched 1.00 J/cm²
4.76 ft-lb/in²
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 240 °C
464 °F
Deflection Temperature at 0.46 MPa (66 psi) >= 300 °C
>= 572 °F
Deflection Temperature at 1.8 MPa (264 psi) >= 300 °C
>= 572 °F
Vicat Softening Point >= 300 °C
<br>@Load 5.00 kg
 >= 572 °F
<br>@Load 11.0 lb
Flammability, UL94 V-1
<br>@Thickness 0.750 mm
 V-1
<br>@Thickness 0.0295 in
V-0
<br>@Thickness 3.00 mm
 V-0
<br>@Thickness 0.118 in
V-0
<br>@Thickness 1.50 mm
 V-0
<br>@Thickness 0.0591 in
Glow Wire Test 875 °C
<br>@Thickness 1.00 mm
 1610 °F
<br>@Thickness 0.0394 in
 GWIT
960 °C
<br>@Thickness 2.00 mm
 1760 °F
<br>@Thickness 0.0787 in
 GWFI/GWT
Processing Properties Metric English Comments
Melt Temperature 370 - 400 °C
698 - 752 °F
Mold Temperature 170 - 200 °C
338 - 392 °F
Drying Temperature 120 - 150 °C
<br>@Time 10800 sec
 248 - 302 °F
<br>@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa