Solvay Specialty Polymers Amodel® AF-1145 V0 Polyphthalamide (PPA) Resin, 45% Glass Reinforced, Dry As Molded  

Category Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), 50% Glass Fiber Reinforced
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers Amodel® AF-1145 V0 Polyphthalamide (PPA) Resin, 45% Glass Reinforced, Dry As Molded  .pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
AMODEL AF-1145 V0 is a 45% glass reinforced, flame retarded polyphthalamide (PPA) which exhibits a high heat distortion temperature, high tensile strength and flexural modulus. The material is relatively insensitive to moisture which results in good dimensional stability. Therefore, typical humid environmental conditions result in only minor changes in the strength and stiffness. This grade of AMODEL resin can withstand the demanding vapor phase and infrared reflow soldering processes typically used in the electronics industry. It is ideally suited for connectors and electrical devices requiring surface mount technology (SMT). The material offers easy processing using conventional equipment and methods.This product line was acquired by Solvay Advanced Polymers from BP Amoco in November 2001.MatWeb has an entry for this material conditioned at 50% RH.
Physical Properties Metric English Comments
Density 1.81 g/cc
0.0654 lb/in³
ASTM D792
Water Absorption 0.17 %
0.17 %
24 hrs. ASTM D570
Linear Mold Shrinkage 0.0020 cm/cm
0.0020 in/in
ASTM E831
Linear Mold Shrinkage, Transverse 0.0040 cm/cm
0.0040 in/in
ASTM E831
Mechanical Properties Metric English Comments
Hardness, Rockwell R 124
124
ASTM D785
Tensile Strength, Ultimate 203 MPa
29400 psi
ASTM D638
Elongation at Break 1.0 %
1.0 %
ASTM D638
Tensile Modulus 18.0 GPa
2610 ksi
ASTM D638
Flexural Yield Strength 283 MPa
41000 psi
ASTM D790
Flexural Modulus 18.0 GPa
2610 ksi
ASTM D790
Izod Impact, Notched 0.640 J/cm
1.20 ft-lb/in
ASTM D256
Izod Impact, Unnotched 6.10 J/cm
11.4 ft-lb/in
ASTM D256
Thermal Properties Metric English Comments
Melting Point 310 °C
590 °F
ASTM D3418
Maximum Service Temperature, Air 140 °C
284 °F
UL746B RTI
Deflection Temperature at 1.8 MPa (264 psi) 275 °C
527 °F
ASTM D648
Flammability, UL94 V-0

@Thickness 0.800 mm
V-0

@Thickness 0.0315 in
V-0

@Thickness 0.800 mm
V-0

@Thickness 0.0315 in
Electrical Properties Metric English Comments
Electrical Resistivity 3.00e+15 ohm-cm
3.00e+15 ohm-cm
ASTM D257
Surface Resistance 2.00e+15 ohm
2.00e+15 ohm
ASTM D257
Dielectric Constant 3.8

@Frequency 100 Hz
3.8

@Frequency 100 Hz
ASTM D150
5.2

@Frequency 1e+6 Hz
5.2

@Frequency 1e+6 Hz
ASTM D150
Dielectric Strength 27.0 kV/mm
686 kV/in
ASTM D149
Dissipation Factor 0.0080

@Frequency 1e+6 Hz
0.0080

@Frequency 1e+6 Hz
ASTM D150
0.010

@Frequency 100 Hz
0.010

@Frequency 100 Hz
ASTM D150
Arc Resistance >= 300 sec
>= 300 sec
UL 746A
Comparative Tracking Index 550 V
550 V
Hot Wire Ignition, HWI >= 150 sec
>= 150 sec
High Amp Arc Ignition, HAI 74 arcs

@Thickness 0.800 mm
74 arcs

@Thickness 0.0315 in
High Voltage Arc-Tracking Rate, HVTR 16.0 mm/min
0.630 in/min
Processing Properties Metric English Comments
Melt Temperature 321 - 338 °C
610 - 640 °F
Injection