Kolon KOPA® KN333HB40HFBL Hybrid Nylon 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | Kolon |
| Trade Name | Kopa® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Kolon KOPA® KN333HB40HFBL Hybrid Nylon 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
High flow, dimensionally stableApplications Fans & ShroudsInformation provided by API-Kolon.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.45 g/cc | 1.45 g/cc | ASTM D792 |
| Moisture Absorption at Equilibrium | 0.40 % | 0.40 % | 60% RH; ASTM D570 |
| Linear Mold Shrinkage | 0.0030 - 0.0050 cm/cm | 0.0030 - 0.0050 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 122 | 122 | ASTM D785 |
| Tensile Strength | 137 MPa | 19900 psi | ASTM D638 |
| Elongation at Break | 6.5 % | 6.5 % | ASTM D638 |
| Flexural Strength | 216 MPa | 31300 psi | ASTM D790 |
| Flexural Modulus | 7.649 GPa | 1109 ksi | ASTM D790 |
| Izod Impact, Notched | 0.540 J/cm | 1.01 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 30.0 µm/m-°C | 16.7 µin/in-°F | ASTM D696 |
| Melting Point | 255 °C | 491 °F | ASTM D1525 |
| Deflection Temperature at 0.46 MPa (66 psi) | 245 °C | 473 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 235 °C | 455 °F | ASTM D648 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 3.4 | 3.4 | ASTM D150 |
| Dielectric Strength | 21.0 kV/mm | 533 kV/in | ASTM D149 |
| Arc Resistance | 135 sec | 135 sec | ASTM D495 |
Users viewing this material also viewed the following:
- LTL Color Compounds ColorFast® FRPBT130 PBT, 30% Glass-Filled
- Solvay TECHNYL® C 216 V15 PA6, 15% glass filled, Eh 50
- Solvay Technyl® C218V30 30% Glass Filled, Heat Stabilized Nylon 6
- SABIC Innovative Plastics LNP THERMOCOMP QC008 PA6.10
- Unitika A1022GFL60 PA6, 60% Glass Fiber Reinforced, Dry
- Hexcel® HexPly® M47 140°C Curing Epoxy Matrix, Woven Carbon Prepreg
- ExxonMobil Exxsol™ D95 Dearomatized Fluid
- Carlson 904L Austenitic Stainless Steel
- Beijing Ranger Chem WSR618 Liquid Epoxy Resin
Copyright © lookpolymers.com All Rights Reserved