Kolon KOPA® KN3321G15VO G/F Reinforced & Flame Retardant Nylon 66

Category	Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Glass Fiber Filled, Flame Retardant
Manufacturer	Kolon
Trade Name	Kopa®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Kolon KOPA® KN3321G15VO G/F Reinforced & Flame Retardant Nylon 66.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

KOPA® is a thermoplastic resin with excellent mechanical, thermal and electrical properties and is widely used in the automobile, electrical and industrial parts.High tensile strength, outstanding self lubrication and abrasion resistance, excellent chemical & weather resistance, high usage temperatureInformation provided by US distributor, API-Kolon.

Physical Properties	Metric	English	Comments
Density	1.43 g/cc	0.0517 lb/in³	DIN 53479; ASTM D792
Water Absorption	0.80 %	0.80 %	DIN 53475; ASTM D570
Linear Mold Shrinkage	0.0050 - 0.010 cm/cm	0.0050 - 0.010 in/in	ASTM D955

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	120	120	DIN 53505; ASTM D785
Tensile Strength, Ultimate	123 MPa	17800 psi	DIN 53455; ASTM D638
Elongation at Break	5.0 %	5.0 %	DIN 53455; ASTM D638
Flexural Yield Strength	196 MPa	28400 psi	DIN 53455; ASTM D790
Flexural Modulus	6.37 GPa	925 ksi	DIN 53452; ASTM D790
Izod Impact, Notched	0.490 J/cm	0.918 ft-lb/in	DIN 53453; ASTM D256

Thermal Properties	Metric	English	Comments
CTE, linear	30.0 µm/m-°C @Temperature 20.0 °C	16.7 µin/in-°F @Temperature 68.0 °F	DIN 53752; ASTM D696
Melting Point	255 °C	491 °F	DIN 53736; ASTM D789
Deflection Temperature at 0.46 MPa (66 psi)	240 °C	464 °F	DIN 53461; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	235 °C	455 °F	DIN 53461; ASTM D648
Flammability, UL94	V-0	V-0

Electrical Properties	Metric	English	Comments
Dielectric Constant	3.6 @Frequency 1e+6 Hz	3.6 @Frequency 1e+6 Hz	ASTM D150/DIN 53483
Dielectric Strength	20.0 kV/mm	508 kV/in	ASTM D149/DIN 53481
Arc Resistance	130 sec	130 sec	ASTM D495

Users viewing this material also viewed the following: