Karina Karintox 70 Polyolefin Compound
| Category | Polymer , Thermoplastic , Polyolefin , Polyolefin, Wire/Cable Grade |
| Manufacturer | Karina Indústria e Comércio de Plásticos |
| Trade Name | Karintox |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Karina Karintox 70 Polyolefin Compound.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Halogen free, fire retardant, low smoke and fume polyolefinic compound. Recommended for insulation of electrical cables up to 1KV.Information provided by Karina Indústria e Comércio de Plásticos Ltda.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.47 - 1.53 g/cc | 1.47 - 1.53 g/cc | ASTM D 792 |
| Moisture Absorption | <= 0.0600 % | <= 0.0600 % | ME-52 |
| ASTM Color | -1.85 - 1.15 | -1.85 - 1.15 | Color A, ME 12 |
| -1.71 - 1.29 | -1.71 - 1.29 | Color B, ME 12 | |
| 78.78 - 81.78 | 78.78 - 81.78 | Color L, ME 12 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 90 - 94 @Time 15.0 sec |
90 - 94 @Time 0.00417 hour |
ASTM D 2240 |
| Tensile Strength | >= 10.0 MPa | >= 1450 psi | After 168 H in Air Oven at 80°C; NBR NM-IEC 60811-1-2 |
| >= 12.6 MPa | >= 1820 psi | NBR NM-IEC 60811-1-1 | |
| Elongation at Break | >= 100 % | >= 100 % | After 168H in Air Oven at 80°C; NBR NM-IEC 60811-1-2 |
| >= 120 % | >= 120 % | NBR NM-IEC 60811-1-1 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Flammability Test | 81 | 81 | % Transmittance - Smoke Density Test; NBR 11300 |
| Oxygen Index | >= 36 % | >= 36 % | ASTM D 2863 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 3.00e+14 ohm-cm | >= 3.00e+14 ohm-cm | ASTM D 257 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Application | 70 Grades | |
| Cold Blend | OK | -15°C; NBR NM-IEC 60811-1-4 |
| Corrosivity of Gases | 4 | pH (NBR 11633) |
| 9,2.00 | Conductivity, mg/g (NBR 11633) | |
| Halogen Acid Gas Evolution (mg/g) | 0 | NBR 10495 |
| Maximum Variation of Elongation (%) | 20 | NBR NM-IEC 60811-1-2 |
| Maximum Variation of Tensile Strength (%) | 20 | NBR NM-IEC 60811-1-2 |
| Toxicity Index | 1,48.00 | NBR 12139 |
Users viewing this material also viewed the following:
- Noble Polymers Ecobarrier™ 0512 Thermoplastic Olefin (TPO)
- Lehmann & Voss LUVOCOM® 1301-0825 PPS, linear, with carbon fiber
- Shinkong Synthetic Fibers Shinite® T101G30 PET, 30% Glass Filled
- Silberline Tufflake® 5950
- SABIC Innovative Plastics NORYL N300X PPE+PS
- Dow Corning SE 1885 KIT
- 3M EC-1 Cold Shrink End Caps
- 3M Scotchcal™ 8000-12 Graphic Film
- DuPont Performance Polymers Delrin® FG100P NC010 Acetal Homopolymer (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved