Kaiser 7068 T6, T651 Rod & Bar
| Category | Metal , Nonferrous Metal , Aluminum Alloy , 7000 Series Aluminum Alloy |
| Manufacturer | Kaiser Aluminum |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Kaiser 7068 T6, T651 Rod & Bar.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Alloy 7068 offers some of the highest strength mechanical properties available in an extruded product. Intended for aerospace, ordnance and light weight recreational applications where extremely high strength is required. Property levels are typically in the 100 ksi range for ultimate strengths.AMS 4331
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 2.85 g/cc | 0.103 lb/in³ |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Brinell | 185 | 185 | 500 kg, 10 mm |
| Tensile Strength, Ultimate | 698 MPa @Diameter 12.7 mm |
101000 psi @Diameter 0.500 in |
|
| Tensile Strength, Yield | 648 MPa @Diameter 12.7 mm |
94000 psi @Diameter 0.500 in |
|
| Elongation at Break | 9.0 % @Diameter 12.7 mm |
9.0 % @Diameter 0.500 in |
4D |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 23.4 µm/m-°C @Temperature 20.0 - 100 °C |
13.0 µin/in-°F @Temperature 68.0 - 212 °F |
|
| Specific Heat Capacity | 1.05 J/g-°C @Temperature 100 °C |
0.250 BTU/lb-°F @Temperature 212 °F |
|
| Melting Point | 476 - 635 °C | 889 - 1180 °F | |
| Solidus | 476 °C | 889 °F | |
| Liquidus | 635 °C | 1180 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Aluminum, Al | 85.48 - 88.85 % | 85.48 - 88.85 % | As Balance |
| Chromium, Cr | <= 0.050 % | <= 0.050 % | |
| Copper, Cu | 1.6 - 2.4 % | 1.6 - 2.4 % | |
| Iron, Fe | <= 0.15 % | <= 0.15 % | |
| Magnesium, Mg | 2.2 - 3.0 % | 2.2 - 3.0 % | |
| Manganese, Mn | <= 0.10 % | <= 0.10 % | |
| Other, each | <= 0.050 % | <= 0.050 % | |
| Other, total | <= 0.15 % | <= 0.15 % | |
| Silicon, Si | <= 0.12 % | <= 0.12 % | |
| Titanium, Ti | <= 0.10 % | <= 0.10 % | |
| Zinc, Zn | 7.3 - 8.3 % | 7.3 - 8.3 % | |
| Zirconium, Zr | 0.050 - 0.15 % | 0.050 - 0.15 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Volumetric CTE m³/m³-K | 0.000068 | 68°F/20°C |
Users viewing this material also viewed the following:
- Plaskolite Optix® CA - 75 UVT General Purpose Acrylic Resin
- Parker Chomerics CHO-SEAL® 6510 Conductive Elastomer
- DuPont Performance Polymers Delrin® FG900P NC010 Acetal Homopolymer (Unverified Data**)
- Gharda Chemicals Gafone™ T6300 Polysupersulfone (PSS) (discontinued **)
- DuPont™ Dartek® N-201 Nylon 6,6 Non-Forming Film, 25 µm Thickness (discontinued **)
- Techmer ES Luriblend® PA6 GL10 Nylon 6
- A. Schulman LP481 Molding Grade High-Density Polyethylene
- ThyssenKrupp XABO® 890 Structural Steel
- Braskem H 107 Coating Polypropylene
- BASF Novolen® 1100 RC Polypropylene, Injection Molding Grade
Copyright © lookpolymers.com All Rights Reserved