International Mold Steel DHA-World Die Cast & Forging Steel
| Category | Metal , Ferrous Metal , Tool Steel |
| Manufacturer | International Mold Steel |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | International Mold Steel DHA-World Die Cast & Forging Steel.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
DHA-World is a high hardenability and high tough general use hot work die steel.Information provided by International Mold Steel
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 7.80 g/cc | 0.282 lb/in³ |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Brinell | <= 229 | <= 229 | |
| Hardness, Rockwell C | <= 53 | <= 53 | |
| Fracture Toughness | 50.0 MPa-m½ | 45.5 ksi-in½ | 47 HRC |
| 80.0 MPa-m½ | 72.8 ksi-in½ | 43 HRC | |
| Charpy Impact Unnotched | 20.0 J/cm² | 95.2 ft-lb/in² | 49 HRC |
| 22.0 J/cm² | 105 ft-lb/in² | 47 HRC | |
| 37.0 J/cm² | 176 ft-lb/in² | 44 HRC |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 11.3 µm/m-°C @Temperature 20.0 - 100 °C |
6.28 µin/in-°F @Temperature 68.0 - 212 °F |
|
| 12.1 µm/m-°C @Temperature 20.0 - 300 °C |
6.72 µin/in-°F @Temperature 68.0 - 572 °F |
||
| 12.8 µm/m-°C @Temperature 20.0 - 500 °C |
7.11 µin/in-°F @Temperature 68.0 - 932 °F |
||
| 13.2 µm/m-°C @Temperature 20.0 - 700 °C |
7.33 µin/in-°F @Temperature 68.0 - 1290 °F |
||
| Specific Heat Capacity | 0.473 J/g-°C @Temperature 100 °C |
0.113 BTU/lb-°F @Temperature 212 °F |
|
| 0.558 J/g-°C @Temperature 300 °C |
0.133 BTU/lb-°F @Temperature 572 °F |
||
| 0.667 J/g-°C @Temperature 500 °C |
0.159 BTU/lb-°F @Temperature 932 °F |
||
| 0.934 J/g-°C @Temperature 700 °C |
0.223 BTU/lb-°F @Temperature 1290 °F |
||
| Thermal Conductivity | 25.2 W/m-K @Temperature 100 °C |
175 BTU-in/hr-ft²-°F @Temperature 212 °F |
|
| 27.6 W/m-K @Temperature 700 °C |
192 BTU-in/hr-ft²-°F @Temperature 1290 °F |
||
| 27.9 W/m-K @Temperature 300 °C |
194 BTU-in/hr-ft²-°F @Temperature 572 °F |
||
| 28.7 W/m-K @Temperature 500 °C |
199 BTU-in/hr-ft²-°F @Temperature 932 °F |
Users viewing this material also viewed the following:
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 20 PHR Atomite Whiting Filler
- Plenco 5314 Black (INJ) Impact Grade Phenolic Molding Compound (discontinued **)
- Indium Corp. Indalloy® 151 Pb-Sn-Ag Solder Alloy
- LG Chemical HF-350 ABS, High Flow, High Impact
- Toyobo TS101 PPS, Glass Fiber/Mineral Reinforced
- A. Schulman PP 1449-01 Polypropylene General-Purpose Homopolymer Polypropylene
- American Elements Niobium Nanoparticles
- Eagle Brass 19210 XP-10 Copper Iron, Extra Hard
- Chesterton ARC SD4i High temperature ceramic reinforced erosion resistant coating
- Carpenter Custom 450® Stainless Steel, 25 mm Bar, Condition H1050 (Age Hardened 566°C)
Copyright © lookpolymers.com All Rights Reserved