- Inno-Comp INNOPOL® CS 3-9120 SR5 17% Talc Filled Polypropylene Blend
Inno-Comp INNOPOL® CS 3-9120 SR5 17% Talc Filled Polypropylene Blend
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 20% Talc Filler |
| Manufacturer | Inno-Comp Ltd |
| Trade Name | INNOPOL® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Inno-Comp INNOPOL® CS 3-9120 SR5 17% Talc Filled Polypropylene Blend.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
INNOPOL® CS 3-9120 SR5 is a 17% talc-filled compound based on blend of polypropylene block copolymer and homopolymer. This grade is available in natural and custom colored form.INNOPOL® CS 3-9120 SR5 is developed for producing injection molded automotive components.Information provided by INNO-COMP
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.02 g/cc | 0.0368 lb/in³ | ISO 1183 |
| Melt Flow | 30 g/10 min @Load 2.16 kg, Temperature 230 °C |
30 g/10 min @Load 4.76 lb, Temperature 446 °F |
nozzle diam 2.095 mm; ISO 1133 |
| Storage Temperature | <= 60.0 °C | <= 140 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 25.0 MPa | 3630 psi | 50 mm/min; ISO 527-1,-2 |
| Elongation at Yield | 3.0 % | 3.0 % | 50 mm/min; ISO 527-1,-2 |
| Tensile Modulus | 2.10 GPa | 305 ksi | 1 mm/min; ISO 527-1,-2 |
| Flexural Modulus | 2.20 GPa | 319 ksi | ISO 178 |
| Charpy Impact, Notched | 0.220 J/cm² @Temperature -20.0 °C |
1.05 ft-lb/in² @Temperature -4.00 °F |
ISO 179/1eA |
| 0.450 J/cm² @Temperature 23.0 °C |
2.14 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 108 °C | 226 °F | ISO 75-1,-2 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 190 - 240 °C | 374 - 464 °F | Injection |
| Middle Barrel Temperature | 190 - 240 °C | 374 - 464 °F | Injection |
| Front Barrel Temperature | 190 - 240 °C | 374 - 464 °F | Injection |
| Melt Temperature | 210 - 250 °C | 410 - 482 °F | Injection |
| Mold Temperature | 10.0 - 50.0 °C | 50.0 - 122 °F | |
| Moisture Content | <= 0.070 % | <= 0.070 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Resin Designation | PP-H/PP-B TD 17 | ISO 1043 |
Users viewing this material also viewed the following:
- Okulen® 2000 PE-UHMW, OF
- Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 4.8 mm thick sheet
- Lord Adhesives Metech 2232 Silver Conductor
- SABIC Innovative Plastics Ultem 1010KM PEI (Europe-Africa-Middle East)
- SABIC Innovative Plastics Valox® VIC4350 PBT (Asia Pacific)
- SABIC Innovative Plastics LNP Thermocomp IF002 PA 6/12
- CP-Polymer-Technik Wellamid® 6000 GVS 20/10 HWCP 20% Glass Fiber and 10% Glass Sphere Nylon 6, Heat Stabilized, Dry
- Eurostar Staramide AST44 PA66, Impact Modified, Injection Molded
- DuPont™ Surlyn® 1702 Zinc Ionomer Resin for Extrusion Coating
- SABIC Innovative Plastics LNP LUBRICOMP DFP34 PC
Copyright © lookpolymers.com All Rights Reserved