Inno-Comp INNOPOL® CS 2-5830 SA 30% Glass Filled Polypropylene Copolymer
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 30% Glass Fiber Filler |
| Manufacturer | Inno-Comp Ltd |
| Trade Name | INNOPOL® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Inno-Comp INNOPOL® CS 2-5830 SA 30% Glass Filled Polypropylene Copolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
INNOPOL® CS 2-5830 SA is a 30 % glass-fiber-filled polypropylene block-copolymer compound. This grade is available in natural and custom colored form.INNOPOL® CS 2-5830 SA is recommended for producing injection molded products, where the required properties are a good stiffness besides excellent impact strength.Information provided by INNO-COMP
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | ISO 1183 |
| Melt Flow | 5.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
5.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
nozzle diam 2.095 mm; ISO 1133 |
| Storage Temperature | <= 60.0 °C | <= 140 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 75.0 MPa | 10900 psi | 50 mm/min; ISO 527-1,-2 |
| Elongation at Yield | 2.5 % | 2.5 % | 50 mm/min; ISO 527-1,-2 |
| Tensile Modulus | 5.50 GPa | 798 ksi | 2 mm/min; ISO 527-1,-2 |
| Charpy Impact, Notched | 1.20 J/cm² @Temperature -20.0 °C |
5.71 ft-lb/in² @Temperature -4.00 °F |
ISO 179/1eA |
| 1.60 J/cm² @Temperature 23.0 °C |
7.61 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 150 °C | 302 °F | ISO 75-1,-2 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 190 - 240 °C | 374 - 464 °F | Injection |
| Middle Barrel Temperature | 190 - 240 °C | 374 - 464 °F | Injection |
| Front Barrel Temperature | 190 - 240 °C | 374 - 464 °F | Injection |
| Melt Temperature | 210 - 250 °C | 410 - 482 °F | Injection |
| Mold Temperature | 15.0 - 50.0 °C | 59.0 - 122 °F | |
| Moisture Content | <= 0.070 % | <= 0.070 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Resin Designation | PP-B GF30 | ISO 1043 |
Users viewing this material also viewed the following:
- Precision Polymer Engineering Perlast® G80T Perfluoroelastomer
- Precision Polymer Engineering Z85L Hydrogenated NBR Compound
- Ravago Manufacturing Americas Enviramid™ N1300STHL Post Consumer Recycle Nylon 66
- Solvay TECHNYLSTARâ„¢ S 60G1 V30 PA6, 30% glass filled, Conditioned
- Master Bond Mastersil 153 Two Component, High Temperature Resistance Silicone Adhesive
- A. Schulman FORMION™ FI 105E Non-Reinforced, Extrusion Grade Sodium Ionomer
- BASF Isobutanol
- LTL Color Compounds ColorFast® FRPC310 Polycarbonate, Flame-Retarded
Copyright © lookpolymers.com All Rights Reserved