Ineos H05A-00 Polypropylene Homopolymer
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | Ineos Olefins & Polymers USA |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ineos H05A-00 Polypropylene Homopolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Grade H05A-00 is an antistatic polypropylene homopolymer for injection molding & extrusion applications. This material meeets the requirements of the U.S. Food and Drug Administration as specified in 21 CFR 177.1520 and is Drug Master file listed.Suggested fabrication methods: Injection molding; ExtrusionFeatures: AntistaticTypical applications: Closures, TubingComplies with FDA specification, Title 21, CFR 177.1520.Typical property data below from injection molded samples.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.886 - 0.926 g/cc | 0.0320 - 0.0335 lb/in³ | ASTM D1505 |
| Water Absorption | <= 0.010 % | <= 0.010 % | 24 hours; ASTM D570 |
| Linear Mold Shrinkage | 0.010 - 0.025 cm/cm | 0.010 - 0.025 in/in | ASTM D955 |
| Melt Flow | 4.7 g/10 min @Load 2.16 kg, Temperature 230 °C |
4.7 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 79 - 108 | 79 - 108 | Normal range for injection molding resins; ASTM D785 |
| Tensile Strength, Yield | 36.0 MPa | 5220 psi | ASTM D638 |
| Elongation at Break | >= 500 % | >= 500 % | ASTM D638 |
| Elongation at Yield | 9.0 % | 9.0 % | ASTM D638 |
| Flexural Modulus | 1.48 GPa | 215 ksi | ASTM D790A |
| Izod Impact, Notched | 0.200 - 0.300 J/cm @Diameter 3.17 mm |
0.375 - 0.562 ft-lb/in @Diameter 0.125 in |
bar; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 65.0 °C | 149 °F | UL Relative Thermal Index |
| Deflection Temperature at 0.46 MPa (66 psi) | 102 °C | 216 °F | ASTM D648 |
| Flammability, UL94 | HB | HB |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Process | Extrusion | |
| Injection Molding | ||
| Region | Mexico | Bamberger Polymers Distribution |
| US & Canada | Bamberger Polymers Distribution |
Users viewing this material also viewed the following:
- Overview of materials for Polyphthalamide (PPA), Carbon Fiber
- Ineos Nova 2580 General Purpose Crystal Polystyrene (discontinued **)
- ExxonMobil 222 Mobilgrease XHP Series
- Wellman EcoLon® MRGF1882-BK1(GPE) Nylon 66, 40% Mineral and Glass Reinforced
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 30 PHR Atomite Whiting Filler
- Dow Corning MOLYKOTE® PG-75 GREASE
- DSM Stanyl® TW200F8 (DAM) Nylon 46 40% Glass Reinforced, Heat Stabilized (North America)
- ExxonMobil LLDPE LL 6101RQ Wire & Cable Linear Low Density Polyethylene Resin (European Grade)
- Dow SPECTRIM™ 50B-S Polyol
- Fainplast Compounds GSK 74/UV Flexible PVC, Injection Molding, Lead Free
Copyright © lookpolymers.com All Rights Reserved