SCG Chemicals EL-Leneâ„¢ H1000PC High Density Polyethylene Pipe Resin
| Category | Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Pipe Grade |
| Manufacturer | SCG Chemicals Co. |
| Trade Name | EL-Lene™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SCG Chemicals EL-Leneâ„¢ H1000PC High Density Polyethylene Pipe Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Key Characteristics: Good processing, high thermal stability, low sagging, good balance of MRS, SCG, and RCPRecommended Applications: Water pressure and gas pipesCertification: Certified by EXOVA, LNE, AENOR, INSTA, GOST, PE100+ associationInformation provided by SCG Chemicals
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.959 g/cc | 0.959 g/cc | ISO 1183 |
| Environmental Stress Crack Resistance | >= 10000 hour | >= 10000 hour | F0; ASTM D1693 |
| Oxidative Induction Time (OIT) | >= 70 min @Temperature 200 °C |
>= 70 min @Temperature 392 °F |
ISO/TR10837 |
| Carbon Black Loading | 2.3 % | 2.3 % | ISO 6964 |
| Melt Flow | 0.25 g/10 min @Load 5.00 kg, Temperature 190 °C |
0.25 g/10 min @Load 11.0 lb, Temperature 374 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 64 | 64 | ASTM D2240 |
| Tensile Strength at Break | 35.0 MPa | 5080 psi | Crosshead speed 100 mm/min; ISO 527 |
| Tensile Strength, Yield | 23.0 MPa | 3340 psi | Crosshead speed 100 mm/min; ISO 527 |
| Elongation at Break | 791 % | 791 % | Crosshead speed 100 mm/min; ISO 527 |
| Flexural Modulus | 1.00 GPa | 145 ksi | ASTM D790 |
| Izod Impact, Notched | 2.45 J/cm @Temperature -20.0 °C |
4.59 ft-lb/in @Temperature -4.00 °F |
ASTM D256 |
| 3.14 J/cm @Temperature 0.000 °C |
5.88 ft-lb/in @Temperature 32.0 °F |
ASTM D256 | |
| 3.53 J/cm @Temperature 23.0 °C |
6.61 ft-lb/in @Temperature 73.4 °F |
ASTM D256 | |
| Hydrostatic Design Basis | 10.0 MPa | 1450 psi | ISO 9080 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Brittleness Temperature | <= -60.0 °C | <= -76.0 °F | ASTM D746 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Carbon Black/Pigment Dispersion (grade) | <3 | ISO 18553 |
| Color | Black | |
| Rapid Crack Propagation | =12 bar | ISO 13477 |
| Resistance to Gas Constituents | >20 hours | ISO 1167 |
| Resistance to Slow Crack Growth | >500 hours | ISO 13479 |
Users viewing this material also viewed the following:
- Polimeri Europa KOBLEND PCA PD 935 G2 PC+ABS, 10% Glass Fiber (discontinued **)
- Northstar Polymers PNA-157 Curing Agent
- Lehmann & Voss LUVOCOM® 1105-7568/GY PEEK, with PTFE
- Styron DL 460NA SB Latex
- Saint-Gobain Meldin® 3140 Thermoplastic Bearing Material
- Hexcel® IM4 Carbon Fiber (12,000 Filaments)
- Borealis Bormod™ BF970MO Polypropylene for Injection Molding
- Dow Corning 175KG-DRUM BLADDER LUBRICANT
- ATI Wah Chang 425™ Titanium Alloy, Tubular Extruded
- DuPont Performance Polymers Minlon® EFE6053 BK413 Nylon 66 (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved