Ineos ABS NOVODUR® KU 2-5296 ABS, Extrusion Grade (discontinued **)

Category	Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Unreinforced, Flame Retardant
Manufacturer
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Ineos ABS NOVODUR® KU 2-5296 ABS, Extrusion Grade (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

Extrusion grade, flame retardant, medium toughness, suitable for thermoforming. Contains no polyhalogenated diphenyls or diphenyl ethers.Applications: Extruded sheets and profiles.Information provided by the manufacturer.Novodur is produced by Styrolution (2014). This grade was discontinued prior to Styrolution's acquisition of the Novodur product line.

Physical Properties	Metric	English	Comments
Density	1.19 g/cc	0.0430 lb/in³
Water Absorption	0.30 %	0.30 %	Saturation in water
Water Absorption at Saturation	0.30 %	0.30 %
Melt Flow	20 g/10 min @Load 10.0 kg, Temperature 220 °C	20 g/10 min @Load 22.0 lb, Temperature 428 °F

Mechanical Properties	Metric	English
Tensile Strength, Yield	45.0 MPa	6530 psi
Elongation at Yield	2.2 %	2.2 %
Tensile Modulus	2.50 GPa	363 ksi

Thermal Properties	Metric	English
CTE, linear, Parallel to Flow	104 µm/m-°C @Temperature 20.0 °C	57.8 µin/in-°F @Temperature 68.0 °F
Deflection Temperature at 0.46 MPa (66 psi)	90.0 °C	194 °F
Deflection Temperature at 1.8 MPa (264 psi)	86.0 °C	187 °F
Vicat Softening Point	88.0 °C	190 °F
Flammability, UL94	V-0 @Thickness 1.60 mm	V-0 @Thickness 0.0630 in
	V-0 @Thickness 3.20 mm	V-0 @Thickness 0.126 in

Electrical Properties	Metric	English
Electrical Resistivity	1.00e+15 ohm-cm	1.00e+15 ohm-cm
Surface Resistance	1.00e+14 ohm	1.00e+14 ohm
Dielectric Constant	2.8 @Frequency 1e+6 Hz	2.8 @Frequency 1e+6 Hz
	3.0 @Frequency 100 Hz	3.0 @Frequency 100 Hz
Dielectric Strength	24.0 kV/mm	610 kV/in
Dissipation Factor	0.0040 @Frequency 100 Hz	0.0040 @Frequency 100 Hz
	0.0070 @Frequency 1e+6 Hz	0.0070 @Frequency 1e+6 Hz
Comparative Tracking Index	450 V	450 V