Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Molded |
Manufacturer | Ineos ABS |
Trade Name | Lustran® |
Port | Shanghai port,China |
Trade Terms | FOB, CFR, CIF |
Payment Terms | L/C, T/T, Western Union |
Download PDF | Ineos ABS Lustran® Elite HH 1827.pdf |
Price | EMAIL US sales@lookpolymers.com |
Physical Properties | Metric | English | Comments |
---|---|---|---|
Density | 1.05 g/cc | 0.0379 lb/in³ | |
Melt Flow | 13 g/10 min @Load 10.0 kg, Temperature 220 °C |
13 g/10 min @Load 22.0 lb, Temperature 428 °F |
cm³/10 min. |
Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 39.3 MPa | 5700 psi | |
Elongation at Break | 25 % | 25 % | Nominal |
Elongation at Yield | 3.5 % | 3.5 % | |
Tensile Modulus | 2.30 GPa | 334 ksi | |
Charpy Impact, Notched | 1.90 J/cm² | 9.04 ft-lb/in² | |
0.600 J/cm² @Temperature -30.0 °C |
2.86 ft-lb/in² @Temperature -22.0 °F |
Thermal Properties | Metric | English | Comments |
---|---|---|---|
CTE, linear, Parallel to Flow | 83.0 µm/m-°C @Temperature 20.0 °C |
46.1 µin/in-°F @Temperature 68.0 °F |
|
Deflection Temperature at 0.46 MPa (66 psi) | 95.0 °C | 203 °F | |
Deflection Temperature at 1.8 MPa (264 psi) | 79.0 °C | 174 °F | |
Vicat Softening Point | 101 °C | 214 °F | 50°C/h 50N |
Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
UL Recognized |
HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
UL Recognized |
Processing Properties | Metric | English | Comments |
---|---|---|---|
Melt Temperature | 250 °C | 482 °F | Injection Molding |
Mold Temperature | 60.0 °C | 140 °F | Injection Molding |
Injection Velocity | 200 mm/sec | 7.87 in/sec | |
Injection Pressure | 55.0 MPa | 7980 psi |