Ineos ABS Lustran® ABS 240 Injection Molding Grade
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Molded |
| Manufacturer | Ineos ABS |
| Trade Name | Lustran® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ineos ABS Lustran® ABS 240 Injection Molding Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Lustran® ABS 240 has standard impact strength and is injection molding grade.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Transverse | 0.0040 - 0.0060 cm/cm | 0.0040 - 0.0060 in/in | ISO 294-4 |
| Melt Flow | 20 g/10 min @Load 10.0 kg, Temperature 220 °C |
20 g/10 min @Load 22.0 lb, Temperature 428 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 115 | 115 | ISO 2039-2 |
| Tensile Strength at Break | 35.0 MPa | 5080 psi | 50 mm/min; ISO 527-1,-2 |
| Tensile Strength, Yield | 49.0 MPa | 7110 psi | 50 mm/min; ISO 527-1,-2 |
| Elongation at Break | 20 % | 20 % | 50 mm/min; acc. ISO 527-1,-2 |
| Tensile Modulus | 2.55 GPa | 370 ksi | 1 mm/min; ISO 527-1,-2 |
| Flexural Strength | 75.0 MPa | 10900 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 2.50 GPa | 363 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² @Temperature -30.0 °C |
3.33 ft-lb/in² @Temperature -22.0 °F |
ISO 180-1A |
| 12.0 kJ/m² @Temperature -20.0 °C |
5.71 ft-lb/in² @Temperature -4.00 °F |
ISO 180-1A | |
| 16.0 kJ/m² @Temperature 23.0 °C |
7.61 ft-lb/in² @Temperature 73.4 °F |
ISO 180-1A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 97.0 °C | 207 °F | ISO 75-1,-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 93.0 °C | 199 °F | ISO 75-1,-2 |
| Vicat Softening Point | 100 °C @Load 5.10 kg |
212 °F @Load 11.2 lb |
120°C/hour; ISO 306 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Gloss | 88 % | 88 % | Angle 60°; ISO 2813 |
Users viewing this material also viewed the following:
- S&E Specialty Polymers GTPO8102/R PVC
- Overview of materials for Styrenic TPE (Unverified Data**)
- KB Alloys 60% Manganese Aluminum Alloy
- Inno-Comp INNOBATCH® PPH 3260 60% Chalk Filled Polypropylene Homopolymer
- Karina E 36/210-GEN Green Brown (SP31456) for PVC
- Haynes Hastelloy® Hybrid-BC1® Nickel Alloy Shielded Metal Arc Welded (SMAW) Plate
- Sibur PVC S-6558-U-LP Suspension Polyvinyl Chloride (PVC)
- Techmer ES Luriblend® PPA CF30 TL15 30% Carbon Filled
- ELASTO UK Dryflex® 500700S SEBS Based Material, Unfilled Qualities, 70A Hardness, Translucent
Copyright © lookpolymers.com All Rights Reserved