Ineos ABS Lustran® 720 ABS, Molding Grade
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Molded |
| Manufacturer | Ineos ABS |
| Trade Name | Lustran® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ineos ABS Lustran® 720 ABS, Molding Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Lustran® ABS 720 resin is a black, virgin injection molding grade of ABS (acrylonitrile butadiene styrene). It is supplied as salt-and-pepper pellets with color concentrate 901802 black. Designed for molded drain, waste, and vent (DWV) fittings, Lustran® ABS 720 resin in color 901802 black meets or exceeds ASTM D 3965 3-2-2-2-2 cell class requirements for ASTM F 628 and D 2661. It is also listed under NSF Standard 14 and CSA Standard B181.1.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | ASTM-D792 |
| Melt Flow | 6.5 g/10 min @Load 10.0 kg, Temperature 220 °C |
6.5 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM-D1238 |
| 10 g/10 min @Load 10.0 kg, Temperature 230 °C |
10 g/10 min @Load 22.0 lb, Temperature 446 °F |
ASTM-D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 38.0 MPa | 5510 psi | ASTM-D638 |
| Tensile Modulus | 2.00 GPa | 290 ksi | ASTM-D638 |
| Izod Impact, Notched | 1.28 J/cm @Thickness 3.20 mm, Temperature -30.0 °C |
2.40 ft-lb/in @Thickness 0.126 in, Temperature -22.0 °F |
ASTM-D256 |
| 2.94 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
5.51 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM-D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 104 °C @Thickness 6.35 mm |
219 °F @Thickness 0.250 in |
Annealed; ASTM-D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 232 - 243 °C | 450 - 469 °F | Injection Molding |
| Mold Temperature | 43.0 - 66.0 °C | 109 - 151 °F | |
| Drying Temperature | 82.0 - 93.0 °C @Time 7200 sec |
180 - 199 °F @Time 2.00 hour |
|
| Moisture Content | <= 0.050 % | <= 0.050 % | |
| Dew Point | <= -29.0 °C | <= -20.2 °F | inlet air |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Injection Pressure | Moderately High to High, Injection Molding | |
| Injection Speed | Moderate to Fast | Injection Molding |
Users viewing this material also viewed the following:
- Plastcom SLOVASTER® B1 GF 20 000/2 PBT, 20% glass fibre
- Petroquimica Triunfo Tritheva® TN 2007 EVA Copolymer
- Lord Adhesives CircuitSAFâ„¢ MA-420 Epoxy Surface Mount Adhesive
- Karina 809-36/467-CRM Brown PVC Compound
- Techmer ES HiFill® PA6/6 GB40 BK 40% Glass Bead Filler
- Polyram RamSter PF321G3 PBT, 15% Glass Fiber, Flame Retardant
- Dow H7012-35RN Polypropylene Homopolymer Resin
- BASF Ethyl Acrylate
- Arkema Group Orgalloy® LE 6006 Nylon Alloy, 6% Glass Fiber Reinforced (Conditioned)
- PolyOne Synprene® ST-6160 Thermoplastic Elastomer - SBC (discontinued **)
Copyright © lookpolymers.com All Rights Reserved