Ineos ABS Centrex® 833 ASA+AES Blend (discontinued **)

Category	Polymer , Thermoplastic , AES Polymer , ASA Polymer , Acrylonitrile/Styrene/Acrylate (ASA), Unreinforced, Molded
Manufacturer
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Ineos ABS Centrex® 833 ASA+AES Blend (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Key Features:UnfilledHigh impact or high impact modifiedLight stabilized or stable to lightU.V. stabilized or stable to weatherSuitable processing methods:Profile extrusionSheet extrusionThermoformingInformation provided by Bayer Polymers.LANXESS was spun-off from Bayer in early 2005. Business renamed Ineos ABS after INEOS acquires a majority shareholding under a JV with Lanxess in 2007. Subsequently Ineos acquired 100% of Ineos ABS.

Physical Properties	Metric	English	Comments
Density	1.05 g/cc	0.0379 lb/in³
Melt Flow	8.3 g/10 min @Load 10.0 kg, Temperature 220 °C	8.3 g/10 min @Load 22.0 lb, Temperature 428 °F	cm³/10 min.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	28.5 MPa	4130 psi
Elongation at Break	50 %	50 %	Nominal
Elongation at Yield	3.0 %	3.0 %
Tensile Modulus	1.87 GPa	271 ksi
Charpy Impact, Notched	3.81 J/cm²	18.1 ft-lb/in²
	1.12 J/cm² @Temperature -30.0 °C	5.33 ft-lb/in² @Temperature -22.0 °F

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	101 µm/m-°C @Temperature 20.0 °C	56.1 µin/in-°F @Temperature 68.0 °F
Deflection Temperature at 0.46 MPa (66 psi)	91.0 °C	196 °F
Deflection Temperature at 1.8 MPa (264 psi)	77.0 °C	171 °F
Vicat Softening Point	93.0 °C	199 °F	50°C/h 50N
Flammability, UL94	HB @Thickness 1.50 mm	HB @Thickness 0.0591 in	UL Recognized
	HB @Thickness 3.00 mm	HB @Thickness 0.118 in	UL Recognized

Electrical Properties	Metric	English	Comments
Dissipation Factor	0.0116 @Frequency 1e+6 Hz	0.0116 @Frequency 1e+6 Hz
	0.0123 @Frequency 100 Hz	0.0123 @Frequency 100 Hz

Processing Properties	Metric	English	Comments
Melt Temperature	250 °C	482 °F	Injection Molding
Mold Temperature	60.0 °C	140 °F	Injection Molding
Injection Velocity	200 mm/sec	7.87 in/sec
Injection Pressure	60.0 MPa	8700 psi