Industrial Laminates/Norplex NP310U Cotton Fabric

Category Polymer , Thermoset , Phenolic
Manufacturer Industrial Laminates/Norplex
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Industrial Laminates/Norplex NP310U Cotton Fabric.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Utility grade canvas phenolic with properties similar to NP310E.Not certifiable to NEMA due to low crosswise flexural strength. Previously designated NP310C.Thickness Tested: 0.062", 0.125", and 0.500"
Physical Properties Metric English Comments
Specific Gravity 1.30 - 1.40 g/cc

@Thickness 1.57 mm
 1.30 - 1.40 g/cc

@Thickness 0.0620 in
 ASTM D792
Moisture Absorption at Equilibrium 2.0 %

@Thickness 1.57 mm
 2.0 %

@Thickness 0.0620 in
 ASTM D229
Mechanical Properties Metric English Comments
Hardness, Rockwell M 90 - 110

@Thickness 1.57 mm
 90 - 110

@Thickness 0.0620 in
 ASTM D785
Tensile Strength, Yield 41.4 MPa

@Thickness 1.57 mm
 6000 psi

@Thickness 0.0620 in
 CW; ASTM D638
51.7 MPa

@Thickness 1.57 mm
 7500 psi

@Thickness 0.0620 in
 LW; ASTM D638
Modulus of Elasticity 6.21 GPa

@Thickness 1.57 mm
 900 ksi

@Thickness 0.0620 in
 LW; ASTM D229
6.89 GPa

@Thickness 1.57 mm
 1000 ksi

@Thickness 0.0620 in
 CW; ASTM D229
Flexural Strength 93.1 MPa

@Thickness 1.57 mm
 13500 psi

@Thickness 0.0620 in
 CW; ASTM D790
159 MPa

@Thickness 1.57 mm
 23000 psi

@Thickness 0.0620 in
 LW; ASTM D790
Compressive Strength 193 MPa

@Thickness 12.7 mm
 28000 psi

@Thickness 0.500 in
 ASTM D695
Shear Strength 89.6 MPa

@Thickness 15.7 mm
 13000 psi

@Thickness 0.620 in
 ASTM D732
Izod Impact, Unnotched 0.534 J/cm

@Thickness 12.7 mm
 1.00 ft-lb/in

@Thickness 0.500 in
 CW, Cond E-48/50; ASTM D256
0.801 J/cm

@Thickness 12.7 mm
 1.50 ft-lb/in

@Thickness 0.500 in
 LW, Cond E-48/50; ASTM D256
Thermal Properties Metric English Comments
CTE, linear 20.0 µm/m-°C

@Thickness 1.57 mm,
Temperature 20.0 °C
 11.1 µin/in-°F

@Thickness 0.0620 in,
Temperature 68.0 °F
 x-axis; IPC-TM 650-2.4.24
CTE, linear, Transverse to Flow 22.0 µm/m-°C

@Thickness 1.57 mm,
Temperature 20.0 °C
 12.2 µin/in-°F

@Thickness 0.0620 in,
Temperature 68.0 °F
 x-axis; IPC-TM 650-2.4.24
Maximum Service Temperature, Air 125 °C
257 °F
Flammability, UL94 HB

@Thickness 1.57 mm
 HB

@Thickness 0.0620 in
Electrical Properties Metric English Comments
Dielectric Strength 21.7 kV/mm

@Thickness 1.57 mm
 550 kV/in

@Thickness 0.0620 in
 Cond A; ASTM D229 S.T.
Dielectric Breakdown 50000 V

@Thickness 1.57 mm
 50000 V

@Thickness 0.0620 in
 Cond A; ASTM D229 S/S
Arc Resistance 15 sec

@Thickness 3.17 mm
 15 sec

@Thickness 0.125 in
 ASTM D495
Comparative Tracking Index 150 V

@Thickness 3.17 mm
 150 V

@Thickness 0.125 in
 ASTM D3638
Descriptive Properties Value Comments
Bond Strength 1900 lb
0.5", ASTM D229
Color Natural, Black