Industeel CLC 1.2316 Prehardened (300HB) and Corrosion Resistant Mold Steel
| Category | Metal , Ferrous Metal , Tool Steel , Mold Steel |
| Manufacturer | Groupe Arcelor |
| Trade Name | CLC |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Industeel CLC 1.2316 Prehardened (300HB) and Corrosion Resistant Mold Steel.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: CLC 1.2316 is a 16%Cr 1% Mo with improved corrosion resistance properties, thanks to the chromium/molybdenum additions. The high cleanliness/homogeneity of the steel makes it specially adapted to fine polishing (mirror finish). This steel is commonly used for mold steel applications including cores, inserts, mold cavities… working or stored in wet environments. This grade is also used for the production of corrosive materials like PVC.Information provided by manufacturer.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 7.75 g/cc | 0.280 lb/in³ |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Brinell | 340 | 340 | Typical, in Longitudinal |
| Tensile Strength, Ultimate | 1135 MPa | 164600 psi | Typical, Longitudinal Direction |
| Tensile Strength, Yield | 950 MPa @Strain 0.200 % |
138000 psi @Strain 0.200 % |
Typical, Longitudinal Direction |
| Elongation at Break | 10 % | 10 % | Typical, Longitudinal Direction |
| Modulus of Elasticity | 207 GPa | 30000 ksi | Typical, in Longitudinal Direction |
| Charpy Impact | 13.0 J | 9.59 ft-lb | Typical (Longitudinal) |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 11.0 µm/m-°C @Temperature 20.0 - 100 °C |
6.11 µin/in-°F @Temperature 68.0 - 212 °F |
|
| 11.1 µm/m-°C @Temperature 20.0 - 200 °C |
6.17 µin/in-°F @Temperature 68.0 - 392 °F |
||
| 11.7 µm/m-°C @Temperature 20.0 - 400 °C |
6.50 µin/in-°F @Temperature 68.0 - 752 °F |
||
| Specific Heat Capacity | 0.460 J/g-°C @Temperature 20.0 °C |
0.110 BTU/lb-°F @Temperature 68.0 °F |
|
| Thermal Conductivity | 24.3 W/m-K @Temperature 20.0 °C |
169 BTU-in/hr-ft²-°F @Temperature 68.0 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Carbon, C | 0.40 % | 0.40 % | |
| Chromium, Cr | 16 % | 16 % | |
| Iron, Fe | 81.285 - 81.32 % | 81.285 - 81.32 % | As remainder |
| Manganese, Mn | 0.90 % | 0.90 % | |
| Molybdenum, Mo | 1.03 % | 1.03 % | |
| Phosphorous, P | <= 0.030 % | <= 0.030 % | |
| Silicon, Si | 0.35 % | 0.35 % | |
| Sulfur, S | <= 0.0050 % | <= 0.0050 % |
Users viewing this material also viewed the following:
- Dielectric Polymers NT-988-2 Overlap Splice Tape (discontinued **)
- Radici Radilon® S RV300R (dry) Nylon 6
- PolyOne Geon™ Vinyl Flexible R277AM Polyvinyl Chloride + NBR (PVC+NBR)
- Flint Hills AP5520-HA Polypropylene Impact Copolymer
- GRECO ISOPAK 525 ABS Resin
- Lanxess Durethan® T 40 ZS 000000 Partially aromatic polyamide
- Sumitomo Bakelite Durez® 22257 Phenolic, Compression Grade
- American Elements Lead Oxide Nanopowder
- Hexcel® HexWeb® HRH-10 - 1/2 - 2.0 Aramid Fiber/Phenolic Resin Honeycomb
- 3M EC-1 Cold Shrink End Caps
Copyright © lookpolymers.com All Rights Reserved