- ITW Devcon Plastic Steel® Metal Repair (A), Dark Grey
ITW Devcon Plastic Steel® Metal Repair (A), Dark Grey
| Category | Polymer , Adhesive , Thermoset |
| Manufacturer | ITW Devcon |
| Trade Name | Plastic Steel® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | ITW Devcon Plastic Steel® Metal Repair (A), Dark Grey.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by ITW Devcon
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 2.33 g/cc | 0.0840 lb/in³ |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 85 | 85 | Cured; ASTM D2240 |
| Tensile Strength at Break | 22.2 MPa | 3220 psi | ASTM D638 |
| Modulus of Elasticity | 5.86 GPa | 850 ksi | ASTM D638 |
| Flexural Strength | 38.6 MPa | 5600 psi | ASTM D790 |
| Compressive Strength | 57.0 MPa | 8260 psi | ASTM D695 |
| Adhesive Bond Strength | 19.3 MPa | 2800 psi | tensile shear; ASTM D1002 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 86.4 µm/m-°C @Temperature 20.0 °C |
48.0 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Thermal Conductivity | 0.573 W/m-K | 3.97 BTU-in/hr-ft²-°F | ASTM C177 |
| Maximum Service Temperature, Air | 121 °C | 250 °F | dry |
| Shrinkage | 0.060 % | 0.060 % | Cured; ASTM D2566 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 67.5 @Frequency 1000 Hz |
67.5 @Frequency 1000 Hz |
ASTM D150 |
| Dielectric Strength | 1.18 kV/mm | 30.0 kV/in | ASTM D149 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 960 min | 16.0 hour | Functional cure |
| Pot Life | 45.0 min @Temperature 23.9 °C |
45.0 min @Temperature 75.0 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Coverage per pound, in² @ 1/4" thickness | 48 | |
| Mix ratio by volume (Resin:Hardener) | 2.5:1 | |
| Mix ratio by weight (Resin:Hardener) | 9:1 |
Users viewing this material also viewed the following:
- PlastiComp Complet® LCF40-PPA Polyphthalamide, 40% Long Carbon Fiber Reinforced
- Lehmann & Voss LUVOCOM® 80-8510 Polyacetal-copolymer, with mineral filler, lubricant modified
- Mateck Cesium Iodide, CsI
- Momentive Performance Materials Ultraglaze® SSG 4000AC Construction Sealant
- SABIC Innovative Plastics Xenoy® IQ1103U PBT+PC (Asia Pacific)
- Teknor Apex Monprene® MP-2564B Thermoplastic Elastomer
- A. Schulman POLYTROPE™ TPP 1008-01 Injection Molding Reactor Grade Olefinic Thermoplastic Elastomer
- Dow Corning DM3 Demulsifier
- BASF Ultramid® A3L HP PA66 (Dry)
- Materion AlBeMet® AM 162 Rolled Sheet, Annealed
Copyright © lookpolymers.com All Rights Reserved