Huntsman PE1507 EVA Film Extrusion  (discontinued **)

Category Polymer , Film , Thermoplastic , Ethylene Vinyl Acetate , Ethylene Vinyl Acetate Copolymer (EVA), Film Grade
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Huntsman PE1507 EVA Film Extrusion  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
5% Vinyl Acetate EVA copolymer and FDA compliantFeatures: Excellent balance of optical and strength, toughness and flexibility at low temperatures, and good heat seal characteristic.Applications: Film extrusion: frozen food and general purpose packaging where toughness is required.FDA Notes: Conforms to FDA regulation 21 CFR 177.1350 under condition of use C through G described in Table 2 of 21 CFR 176.170Film properties based on 1.0 guage (25 µm) thickness; blow-up ratio 2:1.Information provided by Huntsman Corporation
Physical Properties Metric English Comments
Density 0.925 g/cc
0.0334 lb/in³
ASTM D1505
Thickness 25.4 microns
1.00 mil
Melt Flow 2.0 g/10 min
2.0 g/10 min
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Shore D 46
46
ASTM D2240
Tensile Strength, Ultimate 13.0 MPa
1890 psi
ASTM D638
Tensile Strength, Yield 9.00 MPa
1310 psi
ASTM D638
Film Elongation at Break, MD 400 %
400 %
ASTM D882
Film Elongation at Break, TD 500 %
500 %
ASTM D882
Elongation at Break 800 %
800 %
ASTM D638
Modulus of Elasticity 0.207 GPa
30.0 ksi
Secant; ASTM D638
Secant Modulus, MD 0.117 GPa
17.0 ksi
ASTM D882
Secant Modulus, TD 0.138 GPa
20.0 ksi
ASTM D882
Dart Drop 7.09 g/micron
180 g/mil
ASTM D1709
Dart Drop Test 180 g
0.397 lb
ASTM D1709
Film Tensile Strength at Break, MD 23.0 MPa
3340 psi
ASTM D882
Film Tensile Strength at Break, TD 19.0 MPa
2760 psi
ASTM D882
Thermal Properties Metric English Comments
Vicat Softening Point 86.0 °C
187 °F
ASTM D1525
Optical Properties Metric English Comments
Haze 5.0 %
5.0 %
ASTM D1003
Gloss 73 %
73 %
at 45°; ASTM D523
Processing Properties Metric English Comments
Melt Temperature 163 - 177 °C
325 - 351 °F