Huntsman IROGRAN® PS 455-204 TPU-Polyester
| Category | Polymer , Thermoplastic , Polyurethane, TP , Thermoplastic Polyurethane (TPUR), Polyester Grade |
| Manufacturer | Huntsman Corporation |
| Trade Name | IROGRAN® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Huntsman IROGRAN® PS 455-204 TPU-Polyester.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Polyester-based grades with a broad processing window ideally suited for cast, flat die and flown film lines.Information provided by Alliance Polymers
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.19 g/cc | 0.0430 lb/in³ | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 75 | 75 | ASTM D2240 |
| Hardness, Shore D | 31 | 31 | ASTM D2240 |
| Tensile Strength at Break | 34.5 MPa | 5010 psi | ASTM D412 |
| Elongation at Break | 580 % | 580 % | ASTM D412 |
| 50% Modulus | 0.000689 GPa | 0.100 ksi | ASTM D412 |
| 100% Modulus | 0.00117 GPa | 0.170 ksi | ASTM D412 |
| 300% Modulus | 0.00696 GPa | 1.01 ksi | ASTM D412 |
| Rebound | 49 % | 49 % | Bayshore; ASTM D2632 |
| Tear Strength | 63.1 kN/m | 360 pli | ASTM D624 |
| Taber Abrasion, mg/1000 Cycles | 5.0 | 5.0 | ASTM D3389 |
| Abrasion | 84 | 84 | mm<sup>3</sup>; DIN 53516 |
| Compression Set | 31 % @Temperature 22.8 °C, Time 79200 sec |
31 % @Temperature 73.0 °F, Time 22.0 hour |
ASTM D395 |
| 83 % @Temperature 70.0 °C, Time 79200 sec |
83 % @Temperature 158 °F, Time 22.0 hour |
ASTM D395 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 125 - 144 °C | 257 - 291 °F | TMA Melt Range |
| Vicat Softening Point | 59.0 °C | 138 °F | ASTM D1525 |
| Glass Transition Temp, Tg | -36.0 °C | -32.8 °F | Midpoint; ASTM E 1269 |
Users viewing this material also viewed the following:
- Lubrizol Advanced Materials PEARLTHANE® 18VT80 Thermoplastic Polyurethane Elastomer (discontinued **)
- BASF Capron® 8232G 25% Glass-Filled Nylon 6 (Dry) (discontinued **)
- McDanel Advanced Ceramics 99.8% Alumina
- Michelman® Michem® Lube 188F Anionic carnauba/paraffin wax emulsion
- SABIC Innovative Plastics LNP Thermocomp RF0057E PA 66 (Asia Pacific)
- A. Schulman SCHULAMID® 66 GB40 40% Glass Bead Reinforced Nylon 66
- Dow Corning SE 4448 CV KIT PARTS A&B
- Buckeye Polymers BP RPPC 2010 CW Polypropylene, Calcium Filled
- Bhansali Engineering Santron IMS 2007LF SAN Resin
Copyright © lookpolymers.com All Rights Reserved