Huntsman IROGRAN® A 87 H 4615 Polyester-Based TPU-Injection Molding Grade
| Category | Polymer , Thermoplastic , Elastomer, TPE , Polyurethane TPE , Polyurethane, TP , Thermoplastic Polyurethane, Elastomer, Polyester Grade |
| Manufacturer | Huntsman Corporation |
| Trade Name | IROGRAN® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Huntsman IROGRAN® A 87 H 4615 Polyester-Based TPU-Injection Molding Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Introduction: IROGRAN A 87 H 4615 is a thermoplastic polyester- polyurethane for injection molding applications. Additional characteristics of the product are very short cycle times and high dimensional stability Performance Features: Easy demolding Good melt flow High wear resistance High elasticity Dynamically highly loadableApplications: For the production of mining screens, coupling halves, technical parts, cylinders, buffersInformation provided by Huntsman
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.011 cm/cm | 0.011 in/in | ASTM D995 |
| Melt Index of Compound | 50 g/10 min @Load 21.6 kg, Temperature 190 °C |
50 g/10 min @Load 47.6 lb, Temperature 374 °F |
cm<sup>3</sup>/10 min |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 95 | 95 | ASTM D2240 |
| Hardness, Shore D | 35 | 35 | ASTM D2240 |
| Tensile Strength at Break | 45.0 MPa | 6530 psi | DIN 53504 |
| Elongation at Break | 720 % | 720 % | ASTM D412 |
| 100% Modulus | 0.00560 GPa | 0.812 ksi | DIN 53504 |
| 300% Modulus | 0.0111 GPa | 1.61 ksi | DIN 53504 |
| Rebound | 40 % | 40 % | Bayshore; ASTM D2632 |
| Tear Strength | 105 kN/m | 600 pli | ASTM D624 |
| Abrasion | 25 | 25 | [mm<sup>3</sup>]; ISO 4649 |
| Compression Set | 25 % @Temperature 23.0 °C, Time 252000 sec |
25 % @Temperature 73.4 °F, Time 70.0 hour |
ASTM D395 |
| 43 % @Temperature 70.0 °C, Time 86400 sec |
43 % @Temperature 158 °F, Time 24.0 hour |
ASTM D395 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 135 - 185 °C | 275 - 365 °F | Huntsman/TMA |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Transmission, Visible | 90 % | 90 % | transparent; thickness not reported |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 25.0 - 40.0 °C | 77.0 - 104 °F | Extrusion |
| Front Barrel Temperature | 165 - 190 °C | 329 - 374 °F | Extrusion |
| Nozzle Temperature | 170 - 200 °C | 338 - 392 °F | Extrusion |
| 180 - 200 °C | 356 - 392 °F | Injection | |
| Adapter Temperature | 175 - 195 °C | 347 - 383 °F | Extrusion |
| Die Temperature | 175 - 200 °C | 347 - 392 °F | Extrusion |
| Melt Temperature | 170 - 195 °C | 338 - 383 °F | Injection |
| Mold Temperature | 20.0 - 70.0 °C | 68.0 - 158 °F | Injection |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Heating Zone | 175-195°C | Injection |
Users viewing this material also viewed the following:
- Hyosung Topilene S905 PP
- ICO Polymers ICOFLOâ„¢ 510-5050 500 Micron LDPE Powder
- Sylvin Technologies 8999-85 Natural PVC Extrusion Compound
- SABIC Innovative Plastics NORYL NH7111E PPE+HIPS (Asia Pacific)
- A. Schulman POLYBATCH™ Orange 1046E Concentrate Based In Polyethylene
- Unitika M1030DH PA6, Conditioned
- A. Schulman PP 1349 Polypropylene Medium Impact Copolymer Polypropylene
- Covestro Desmopan® DP 9659DU Polyurethane
- BiologiQ ESR-PE EcoStarch mLLDPE Blend
Copyright © lookpolymers.com All Rights Reserved