Huntsman IROGRAN® A 80 P 4699L Ether-Based TPU-For Cable Industry
| Category | Polymer , Thermoplastic , Elastomer, TPE , Polyurethane TPE , Polyurethane, TP , Thermoplastic Polyurethane, Elastomer, Ether Grade |
| Manufacturer | Huntsman Corporation |
| Trade Name | IROGRAN® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Huntsman IROGRAN® A 80 P 4699L Ether-Based TPU-For Cable Industry.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Introduction: IROGRAN A 80 P 4699 L is a high performance polyether based thermoplastic polyurethane intended for extrusion and injection mold applications. IROGRAN A 80 P 4699 L is part of the HUNTSMAN extrusion / injection mold product range. Performance Features: Good melt flow Low adhesion surface High flexibility Good processability Soft Information provided by Huntsman
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.09 g/cc | 1.09 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0011 cm/cm | 0.0011 in/in | |
| Melt Index of Compound | 140 g/10 min @Load 10.0 kg, Temperature 190 °C |
140 g/10 min @Load 22.0 lb, Temperature 374 °F |
cm<sup>3</sup>/10 min |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 80 | 80 | ASTM D2240 |
| Tensile Strength at Break | 30.0 MPa | 4350 psi | DIN 53504 |
| Elongation at Break | 670 % | 670 % | DIN 53504 |
| 100% Modulus | 0.00570 GPa | 0.827 ksi | DIN 53504 |
| 300% Modulus | 0.00840 GPa | 1.22 ksi | DIN 53504 |
| Rebound | 46 % | 46 % | Bayshore; ASTM D2632 |
| Tear Strength | 76.0 kN/m | 434 pli | DIN 5315 |
| Abrasion | 50 | 50 | mm<sup>3</sup>; DIN 53516 |
| Compression Set | 24 % @Temperature 23.0 °C, Time 79200 sec |
24 % @Temperature 73.4 °F, Time 22.0 hour |
ASTM D395 |
| 46 % @Temperature 70.0 °C, Time 79200 sec |
46 % @Temperature 158 °F, Time 22.0 hour |
ASTM D395 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 175 °C | 347 °F | Extrusion |
| Front Barrel Temperature | 180 °C | 356 °F | Extrusion |
| Adapter Temperature | 180 °C | 356 °F | Extrusion |
| Die Temperature | 175 °C | 347 °F | Extrusion |
Users viewing this material also viewed the following:
- MV Labs BE1005 Be4O(C2H3O2)6 Beryllium acetate basic
- Pacific Sintered Materials FN-253-T(HT) 4600 Powdered Metal
- Quadrant EPP Ketron® 1000 PEEK, Extruded Unfilled Polyetherether Ketone (ASTM Product Data Sheet)
- LATI Laramid G/45 PPA, 45% Glass Fiber Reinforced
- Techmer ES Luriblend® PA6 CF30 TL15 BK 30% Carbon Filled
- Saint-Gobain Tygon® S3™ B-44-4X I.B. Pressure Tubing Formulation for filling, draining, transfer and processing applications
- A. Schulman POLYBLAK™ 4479-01A Black Color Concentrate, 50% Carbon Black Based In Polyethylene
- Fainplast Compounds GS 6520 Flexible PVC, Injection Molding for Footwear
- Ascend Performance Materials Vydyne® 49H NT Nylon 66, Impact Modified, Conditioned
Copyright © lookpolymers.com All Rights Reserved