Huntsman AVALON® 95 AE Thermoplastic Polyurethane
| Category | Polymer , Thermoplastic , Polyurethane, TP , Thermoplastic Polyurethane (TPUR), Polyester Grade |
| Manufacturer | Huntsman Corporation |
| Trade Name | Avalon® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Huntsman AVALON® 95 AE Thermoplastic Polyurethane.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Introduction: AVALON 95 AE is a general purpose polyester based thermoplastic polyurethane for injection molding. AVALON 95 AE is part of the AVALON Perform Range and offers a premium soiling material for sports footwear and top-pieces. The features offered include:DurabilityExcellent surface definitionAbrasion resistanceFlex resistancePhthalate free TPU Information provided by Alliance Polymers
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.24 g/cc | 0.0448 lb/in³ | ISO 2781 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 95 | 95 | ISO 868 |
| Hardness, Shore D | 50 | 50 | ISO 868 |
| Tensile Strength at Break | 33.0 MPa | 4790 psi | ISO 37 |
| Elongation at Break | 400 % | 400 % | ISO 37 |
| 100% Modulus | 0.0110 GPa | 1.60 ksi | ISO 37 |
| 300% Modulus | 0.0180 GPa | 2.61 ksi | ISO 37 |
| Tear Strength | 130 kN/m | 742 pli | ISO 34B |
| Abrasion | 35 | 35 | mm<sup>3</sup>; ISO 4649 |
| Compression Set | 20 % | 20 % | ISO 815 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 25.0 - 35.0 °C | 77.0 - 95.0 °F | |
| Rear Barrel Temperature | 185 - 195 °C | 365 - 383 °F | |
| Middle Barrel Temperature | 190 - 200 °C | 374 - 392 °F | |
| Front Barrel Temperature | 195 - 205 °C | 383 - 401 °F | |
| Nozzle Temperature | 180 - 190 °C | 356 - 374 °F | |
| Mold Temperature | 25.0 - 50.0 °C | 77.0 - 122 °F | |
| Injection Pressure | 2.00 - 10.0 MPa | 290 - 1450 psi | |
| Hold Pressure | 1.00 - 5.00 MPa | 145 - 725 psi | |
| Back Pressure | 0.0300 - 0.300 MPa | 4.35 - 43.5 psi | |
| Screw Speed | 20 - 80 rpm | 20 - 80 rpm |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Compression Ratio | 2-3:1 | |
| L/D Ratio | 20-25:1 | |
| Ross Flex | -10°C, BS 5131 | |
| Typical Screw Diameter | 40-120 nm |
Users viewing this material also viewed the following:
- Niche Polymer PPCG20BK Copolymer PP, 20% Glass Fiber Filled
- Northstar Polymers MAP-R06C Semi Rigid Structural Foam Formulation
- PolyOne Nymax™ GF 1880 33 HS NATURAL Nylon 6/12, Glass Filled (discontinued **)
- BASF Capron® 8200CQ Blend Nylon 6 (Dry) (discontinued **)
- Fine Organics FINALUX G 301 Lubricant Additive
- Mitsubishi Xantar® 22 R Polycarbonate
- Latrobe Lescalloy® AF 1410 VIM-VAR ; 17 in High Strength Alloy Steel
- Indium Corp. 16-1081 Flux Thinner
- Intercontinental Polymers HoPET 728-02 HoPET Polymer Type - Clear, Polyester Pellets
- Goodfellow Platinum 87/Rhodium 13Thermocouple Alloy
Copyright © lookpolymers.com All Rights Reserved