Honeywell Capran® Emblem™ 2500 Bi-Axially Oriented Nylon Film
| Category | Polymer , Film , Thermoplastic , Nylon |
| Manufacturer | Honeywell |
| Trade Name | Capran® Emblem™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Honeywell Capran® Emblem™ 2500 Bi-Axially Oriented Nylon Film.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Capran® Emblem™ 2500 is a bi-axially oriented nylon film. It is a versatile and robust film that satisfies many packaging needs, and has superior resistance to oils, fats, hydrocarbons, and many solvents. It is also microwavable, making it an excellent choice for lidding stock.Applications: bag-on-box packaging, packaging for processed meats, cheese, meat snacks, coffee bricks, coffee bags, and pet food, agricultural bags, stand-up shampoo pouches, book covers and metallized balloons.Information provided by Honeywell.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.16 g/cc | 0.0420 lb/in³ | Yield Density |
| Water Vapor Transmission | 171 - 202 g/m²/day | 11.0 - 13.0 g/100 in²/day | 100°F / 100%RH); ASTM F1249 |
| Oxygen Transmission Rate | 20.18 - 35.7 cc/m²/day | 1.300 - 2.30 cc/100 in²/day | 77°F / 0% / RH; ASTM D3985 |
| Thickness | 25.4 microns | 1.00 mil |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Elongation at Break, MD | 70 - 110 % | 70 - 110 % | ASTM D882 |
| Film Elongation at Break, TD | 60 - 90 % | 60 - 90 % | ASTM D882 |
| Secant Modulus, MD | 2.41 - 3.55 GPa | 350 - 515 ksi | ASTM D882 |
| Secant Modulus, TD | 2.275 - 3.28 GPa | 330.0 - 476 ksi | ASTM D882 |
| Coefficient of Friction | 0.21 - 0.41 | 0.21 - 0.41 | film to stainless steel; ASTM D1894 |
| 0.65 - 0.86 | 0.65 - 0.86 | film to film; ASTM D1894 | |
| Tear Strength Test | 1100 - 1400 | 1100 - 1400 | graves tear, grams/mil (initial); ASTM D1004 |
| Elmendorf Tear Strength, MD | 0.591 - 0.748 g/micron | 15.0 - 19.0 g/mil | |
| Film Tensile Strength at Break, MD | 234 - 283 MPa | 34000 - 41000 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 221 - 283 MPa | 32000 - 41000 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Shrinkage, MD | 1.6 - 2.3 % | 1.6 - 2.3 % | 320°F / 160°C - 5 minutes; ASTM D1204 |
| Shrinkage, TD | 0.20 - 0.70 % | 0.20 - 0.70 % | 320°F / 160°C - 5 minutes; ASTM D1204 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | <= 3.4 % | <= 3.4 % | ASTM D1003 |
| Gloss | 90 - 140 % | 90 - 140 % | at 20° |
Users viewing this material also viewed the following:
- Plastcom PLASTAMID® 6 GF 30 005 PA6 reinforced with glass fiber
- Nylene® Vexel™ B12GF45 SA , 45% Glass Reinforced PBT
- Iran Petrochemical (PCC) X 30 G Polypropylene
- Solvay Specialty Polymers Cogegum® AFR/710 Polyolefin
- Samsung Cheil Industries Starex® SR-7300 ABS/PET, Unreinforced
- CeramTec Sikor® E Cordierite
- Eurotec® Tecopet® PT70 GR45 NL100 PR PET, 45% glass fiber reinforced, heat stabilized, natural, fast crystallization grade
- Bulk Molding Compounds BMC T60-6002-WG(15) Wear Resistant Molding Compound
- Performance Polymers IPS II PPL-C1050 PEKK (Polyetherketoneketone) Linear Extrusion Grade
Copyright © lookpolymers.com All Rights Reserved