Hexcel® HexPly® M65 Bismaleimide Resin, Carbon Tape Form

Category	Polymer , Thermoset , Polyimide, TS
Manufacturer	Hexcel
Trade Name	HexPly®
Port	Shanghai port,China
Trade Terms	EXW, FOB, CFR, CIF
Payment Terms	L/C, T/T, PayPal
Download PDF	Hexcel® HexPly® M65 Bismaleimide Resin, Carbon Tape Form.pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

Fiber: IM7-12KInformation provided by HexCel

Physical Properties	Metric	English	Comments
Density	1.56 g/cc	0.0564 lb/in³	Laminate
Volatiles	<= 2.0 %	<= 2.0 %	Prepreg

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	1579 MPa <br>@Temperature 23.0 °C	229000 psi <br>@Temperature 73.4 °F
Elongation at Yield	1.73 % <br>@Temperature 23.0 °C	1.73 % <br>@Temperature 73.4 °F
Tensile Modulus	85.4 GPa <br>@Temperature 23.0 °C	12400 ksi <br>@Temperature 73.4 °F
Flexural Yield Strength	758 MPa <br>@Temperature 177 °C	110000 psi <br>@Temperature 351 °F	IM7 (12K); [0°, 90°]5s; Wet condition
	938 MPa <br>@Temperature 232 °C	136000 psi <br>@Temperature 450 °F	IM7 (12K); [0°, 90°]5s
	1172 MPa <br>@Temperature 23.0 °C	170000 psi <br>@Temperature 73.4 °F
Flexural Modulus	90.7 GPa <br>@Temperature 177 °C	13200 ksi <br>@Temperature 351 °F	IM7 (12K); [0°, 90°]5s; Wet condition
	92.7 GPa <br>@Temperature 232 °C	13400 ksi <br>@Temperature 450 °F	IM7 (12K); [0°, 90°]5s
	94.7 GPa <br>@Temperature 23.0 °C	13700 ksi <br>@Temperature 73.4 °F
Compressive Yield Strength	181 MPa <br>@Temperature 23.0 °C	26300 psi <br>@Temperature 73.4 °F
	696 MPa <br>@Temperature 177 °C	101000 psi <br>@Temperature 351 °F	IM7 (12K); [90°, 0°]2s; Wet condition
	1048 MPa <br>@Temperature 232 °C	152000 psi <br>@Temperature 450 °F	IM7 (12K); [90°, 0°]2s
	1234 MPa <br>@Temperature 23.0 °C	179000 psi <br>@Temperature 73.4 °F
Shear Modulus	2.10 GPa <br>@Temperature 177 °C	305 ksi <br>@Temperature 351 °F	IM7 (12K); [+/- 45°]2s; In Plane; Wet condition
	3.10 GPa <br>@Temperature 232 °C	450 ksi <br>@Temperature 450 °F	IM7 (12K); [+/- 45°]2s; In Plane
	4.70 GPa <br>@Temperature 23.0 °C	682 ksi <br>@Temperature 73.4 °F
Shear Strength	41.0 MPa <br>@Temperature 177 °C	5950 psi <br>@Temperature 351 °F	IM7 (12K); [0°, 90°]5s; Short Beam; Wet condition
	58.7 MPa <br>@Temperature 232 °C	8510 psi <br>@Temperature 450 °F	IM7 (12K); [0°, 90°]5s; Short Beam
	72.0 MPa <br>@Temperature 177 °C	10400 psi <br>@Temperature 351 °F	IM7 (12K); [+/- 45°]2s; In Plane; Wet condition
	80.9 MPa <br>@Temperature 23.0 °C	11700 psi <br>@Temperature 73.4 °F
	82.0 MPa <br>@Temperature 232 °C	11900 psi <br>@Temperature 450 °F	IM7 (12K); [+/- 45°]2s; In Plane
	129 MPa <br>@Temperature 23.0 °C	18700 psi <br>@Temperature 73.4 °F

Descriptive Properties	Value	Comments
Cured Thickness per Ply (cm)	0.0137	Laminate
Dry Resin Content (%)	33	Prepreg
Fiber Volume (%)	59	Laminate