Hexcel® HexPly® M49 120°C Curing Epoxy Matrix, HTA

Category Polymer , Thermoset , Epoxy , Epoxy Cure Resin
Manufacturer Hexcel
Trade Name HexPly®
Port Ningbo port,China
Trade Terms EXW, FOB, CFR, CIF
Payment Terms L/C, T/T, PayPal
Download PDF Hexcel® HexPly® M49 120°C Curing Epoxy Matrix, HTA.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Fiber Designation: C193PW, Plain weaveInformation provided by HexCel
Mechanical Properties Metric English Comments
Tensile Strength, Yield 940 MPa
<br>@Temperature 23.0 °C
 136000 psi
<br>@Temperature 73.4 °F
 0°, Conditioning: 23°C; ASTM D3039
Tensile Modulus 57.0 GPa
<br>@Temperature 23.0 °C
 8270 ksi
<br>@Temperature 73.4 °F
 0°, Conditioning: 23°C; ASTM D3039
Flexural Yield Strength 672 MPa
<br>@Temperature 90.0 °C
 97500 psi
<br>@Temperature 194 °F
 0°, Conditioning: 23°C; ASTM D790
946 MPa
<br>@Temperature 23.0 °C
 137000 psi
<br>@Temperature 73.4 °F
 0°, Conditioning: 23°C; ASTM D790
Flexural Modulus 37.0 GPa
<br>@Temperature 90.0 °C
 5370 ksi
<br>@Temperature 194 °F
 0°, Conditioning: 23°C; ASTM D790
40.0 GPa
<br>@Temperature 23.0 °C
 5800 ksi
<br>@Temperature 73.4 °F
 0°, Conditioning: 23°C; ASTM D790
Compressive Yield Strength 419 MPa
<br>@Temperature 90.0 °C
 60800 psi
<br>@Temperature 194 °F
 0°, Conditioning: 23°C; ASTM D965
592 MPa
<br>@Temperature 23.0 °C
 85900 psi
<br>@Temperature 73.4 °F
 0°, Conditioning: 23°C; ASTM D965
Shear Strength 40.0 MPa
<br>@Temperature 60.0 °C
 5800 psi
<br>@Temperature 140 °F
 0°, Interlaminar, Conditioning: 60°C-90% RH; ASTM D2344
43.0 MPa
<br>@Temperature 90.0 °C
 6240 psi
<br>@Temperature 194 °F
 0°, Interlaminar, Conditioning: 23°C; ASTM D2344
66.0 MPa
<br>@Temperature 23.0 °C
 9570 psi
<br>@Temperature 73.4 °F
 0°, Interlaminar, Conditioning: 23°C; ASTM D2344
Processing Properties Metric English Comments
Shelf Life 12.0 Month
<br>@Temperature -18.0 °C
 12.0 Month
<br>@Temperature -0.400 °F
Descriptive Properties Value Comments
Dry Resin Content (%) 42
Fiber Volume (%) 49.5