- Hexcel® HexPly® F593 Epoxy Resin, F3T584 Carbon Fabric
Hexcel® HexPly® F593 Epoxy Resin, F3T584 Carbon Fabric
| Category | Polymer , Thermoset , Carbon Fiber/Thermoset Composite , Epoxy , Epoxy/Carbon Fiber Composite |
| Manufacturer | Hexcel |
| Trade Name | HexPly® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Hexcel® HexPly® F593 Epoxy Resin, F3T584 Carbon Fabric.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Hexcel designation: F3T584-42"-F593; Fiber: Toray T-300/3kInformation provided by HexCel
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Volatiles | 1.0 - 6.0 % | 1.0 - 6.0 % | Prepreg |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 508 MPa @Temperature -54.0 °C |
73700 psi @Temperature -65.2 °F |
Dry |
| 513 MPa @Temperature 71.0 °C |
74400 psi @Temperature 160 °F |
Wet | |
| 563 MPa @Temperature 24.0 °C |
81700 psi @Temperature 75.2 °F |
Dry | |
| 581 MPa @Temperature 71.0 °C |
84300 psi @Temperature 160 °F |
Dry | |
| Tensile Modulus | 52.4 GPa @Temperature 71.0 °C |
7600 ksi @Temperature 160 °F |
Wet |
| 53.8 GPa @Temperature 71.0 °C |
7800 ksi @Temperature 160 °F |
Dry | |
| 55.9 GPa @Temperature 24.0 °C |
8110 ksi @Temperature 75.2 °F |
Dry | |
| 57.9 GPa @Temperature -54.0 °C |
8400 ksi @Temperature -65.2 °F |
Dry | |
| Compressive Yield Strength | 357 MPa @Temperature 71.0 °C |
51800 psi @Temperature 160 °F |
Wet |
| 398 MPa @Temperature 71.0 °C |
57700 psi @Temperature 160 °F |
Dry | |
| 516 MPa @Temperature 24.0 °C |
74800 psi @Temperature 75.2 °F |
Dry | |
| 641 MPa @Temperature -59.0 °C |
93000 psi @Temperature -74.2 °F |
Dry | |
| Compressive Modulus | 46.9 GPa @Temperature 71.0 °C |
6800 ksi @Temperature 160 °F |
Dry |
| 51.7 GPa @Temperature 24.0 °C |
7500 ksi @Temperature 75.2 °F |
Dry | |
| 57.9 GPa @Temperature -59.0 °C |
8400 ksi @Temperature -74.2 °F |
Dry |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Cured Thickness per Ply (cm) | 0.039-0.046 | Laminate |
| Dry Resin Content (%) | 38-46 | Prepreg |
| Fiber Volume (%) | 45-53 | Laminate |
| Flow (%) | <4.5 |
Users viewing this material also viewed the following:
- NOVA Chemicals Sclair® 8107 UV8D Butene LLDPE Rotational Molding Resin
- Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 4.8 mm thick sheet
- Iran Petrochemical (PCC) 6040UA High Density Polyethylene
- Solvay Specialty Polymers Radel® R-7400 Polyphenylsulfone (PPSU)
- Solvay TECHNYL® 2412GHF6 PA66, 33% glass fiber, Conditioned
- A. Schulman POLYBATCH™ Dark Grey LL80362/4 Concentrate Based In LLDPE
- DuPont Teijin Films Mylar® A Polyester Film, 200 Gauge
- Buckeye Polymers BP FLEX D6509 CU BLK Thermoplastic Polyolefin
- Ascend Performance Materials Vydyne® R533T Nylon 66, Translucent, 33% Glass Filled, Dry as Molded
- Quadrant EPP Sanalite® PP, Homopolymer Polypropylene Cutting Board (FDA, USDA, & NSF) (ASTM Product Data Sheet)
Copyright © lookpolymers.com All Rights Reserved