- Hexcel® HexPly® 954-3A Curing Cyanate Resin, M55J Fiber
Hexcel® HexPly® 954-3A Curing Cyanate Resin, M55J Fiber
| Category | Polymer , Thermoset , Epoxy |
| Manufacturer | Hexcel |
| Trade Name | HexPly® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Hexcel® HexPly® 954-3A Curing Cyanate Resin, M55J Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by HexCel
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 2027 MPa @Temperature 23.0 °C |
294000 psi @Temperature 73.4 °F |
0° |
| Tensile Modulus | 323 GPa @Temperature 23.0 °C |
46800 ksi @Temperature 73.4 °F |
0° |
| Flexural Yield Strength | 928 MPa @Temperature 23.0 °C |
135000 psi @Temperature 73.4 °F |
|
| Flexural Modulus | 263 GPa @Temperature 23.0 °C |
38100 ksi @Temperature 73.4 °F |
|
| Compressive Yield Strength | 896 MPa @Temperature 23.0 °C |
130000 psi @Temperature 73.4 °F |
|
| Compressive Modulus | 302 GPa @Temperature 23.0 °C |
43800 ksi @Temperature 73.4 °F |
|
| Shear Modulus | 3.70 GPa | 537 ksi | In-Plane |
| Shear Strength | 48.0 MPa | 6960 psi | In-Plane |
Users viewing this material also viewed the following:
- Menzolit Menzolit® SMC 0410 Unsaturated Polyester UP
- Inno-Comp INNOPOL® CS 2-9120 20% Talc-Filled Polypropylene Block-Copolymer
- Lucite International Diakon® CLG356 Acrylic Polymer
- LG Chemical EM600 Impact modifier for Engineering Plastics
- Haynes Hastelloy® C-22® alloy, 20% cold worked sheet, aged 100 hours at 500°C
- Solvay MIRATAINE® BET CU Surfactant
- Weartech International WT-700 Nickel Hardfacing & Wear Resistant Alloy
- Ashley Polymers Ashlene® PB1410 Polycarbonate, 10% Glass Reinforced
- BorsodChem ONGROVIL S-494 Suspension PVC-Resin
Copyright © lookpolymers.com All Rights Reserved