- SABIC Innovative Plastics LNP LUBRICOMP Noryl_NF1520 PPE+PS
SABIC Innovative Plastics LNP LUBRICOMP Noryl_NF1520 PPE+PS
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP Noryl_NF1520 PPE+PS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Lubricomp* Noryl_NF1520 compound is a 20% glass reinforced, 15% PTFE. Wear resistant; 211F HDT @ 264 psi.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.34 g/cc | 1.34 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0015 - 0.0025 cm/cm @Thickness 3.20 mm |
0.0015 - 0.0025 in/in @Thickness 0.126 in |
SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0025 - 0.0045 cm/cm @Thickness 3.20 mm |
0.0025 - 0.0045 in/in @Thickness 0.126 in |
SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 74.0 MPa | 10700 psi | Type I, 5 mm/min; ASTM D638 |
| Tensile Strength, Yield | 74.0 MPa | 10700 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 4.2 % | 4.2 % | Type I, 5 mm/min; ASTM D638 |
| Flexural Yield Strength | 101 MPa | 14600 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
| Flexural Modulus | 5.30 GPa | 769 ksi | 2.6 mm/min, 100 mm span; ASTM D790 |
| Izod Impact, Notched | 0.740 J/cm | 1.39 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 3.57 J/cm | 6.69 ft-lb/in | ASTM D4812 |
| Dart Drop, Total Energy | 16.0 J @Temperature 23.0 °C |
11.8 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Coefficient of Friction, Dynamic | 0.46 | 0.46 | steel; ASTM D1894 |
| Coefficient of Friction, Static | 0.30 | 0.30 | steel; ASTM D1894 |
| K (wear) Factor | 147 x 10-8 mm³/N-M | 73.0 x 10-10 in³-min/ft-lb-hr | PV=2000 psi-fpm vs Self; SABIC Method |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 102 °C @Thickness 3.20 mm |
216 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| 105 °C @Thickness 6.40 mm |
221 °F @Thickness 0.252 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 96.0 °C @Thickness 3.20 mm |
205 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| 99.0 °C @Thickness 6.40 mm |
210 °F @Thickness 0.252 in |
unannealed; ASTM D648 | |
| UL RTI, Electrical | 50.0 °C | 122 °F | UL 746B |
| UL RTI, Mechanical with Impact | 50.0 °C | 122 °F | UL 746B |
| UL RTI, Mechanical without Impact | 50.0 °C | 122 °F | UL 746B |
| Flammability, UL94 | HB @Thickness 1.49 mm |
HB @Thickness 0.0587 in |
UL 94 |
Users viewing this material also viewed the following:
- Multibase Nylex™ 2112 FR V0 Natural Polyamide + PP
- Eastman 184MF Polyethylene Film (discontinued **)
- Haysite 14200 Polyester BMC, 15% Glass Reinforced
- SABIC Innovative Plastics Ultem 1000M PEI
- Styron XZ 92091.01 Cross-Linking SB
- A. Schulman POLYFORT™ FXP 1227U UV Stable Copolymer Polypropylene
- ExxonMobil Teresstic N Series 220
- Eagle Brass 70265 XP175, Hard
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 40 PHR Hi-Sil 243 LD Filler
- 3M Dyneon™ PVDF 32008/0003 Polyvinylidene Fluoride (discontinued **)
Copyright © lookpolymers.com All Rights Reserved