Hexcel® HexPly® 920CX-EP2015-47.5% 125°C Curing Epoxy Matrix
| Category | Polymer , Thermoset , Epoxy , Epoxy Cure Resin |
| Manufacturer | Hexcel |
| Trade Name | HexPly® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Hexcel® HexPly® 920CX-EP2015-47.5% 125°C Curing Epoxy Matrix.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Intermediate modulus, 6K carbon, 2x2 twill, 193 g/m2Information provided by HexCel
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 1337 MPa | 193900 psi | pr EN 2561 Type B |
| Tensile Modulus | 87.0 GPa | 12600 ksi | Results normalized to 60% fibre volume for Carbon, 50% fibre volume for Kevlar; pr EN 2561 Type B |
| Compressive Yield Strength | 369 MPa | 53500 psi | Compression After Impact @ 6.6 J/mm, Results normalized to 60% fibre volume for Carbon, 50% fibre volume for Kevlar; pr EN 6038 |
| 901 MPa | 131000 psi | Results normalized to 60% fibre volume for Carbon, 50% fibre volume for Kevlar; EFA TP-003 | |
| Shear Strength | 71.0 MPa | 10300 psi | IL; pr EN 2563 |
Users viewing this material also viewed the following:
- Poco Graphite ZXF-5Q Industrial Grade Graphite
- PTS Trimid® N66-G13 13% Glass Fiber Reinforced Nylon 6/6
- Potters Industries Sphericel® 110P8 Hollow Glass Spheres
- Overview of materials for Nylon 66, Glass Reinforced, Impact Grade
- LG Chemical SEETEC EF320 Ethylene Vinyl Acetate
- H.C. Starck Amperit® 703.072 Chromium Oxide (Cr2O3) 99.5%
- Haynes Hastelloy® C-22® alloy, 10% cold worked sheet, aged 100 hours at 500°C
- Solvay TECHNYL® C 218 V 30 PA6, 30% glass fiber, Conditioned
- Eastman Tritan TX1500HF Copolyester
Copyright © lookpolymers.com All Rights Reserved