Hexcel® HexPly® 8552 Epoxy Matrix, A193-PW Fiber

Category Polymer , Thermoset , Epoxy , Epoxy Cure Resin
Manufacturer Hexcel
Trade Name HexPly®
Port Shanghai port,China
Trade Terms EXW, FOB, CFR, CIF
Payment Terms L/C, T/T, PayPal
Download PDF Hexcel® HexPly® 8552 Epoxy Matrix, A193-PW Fiber.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Information provided by HexCel
Mechanical Properties Metric English Comments
Tensile Strength, Yield 710 MPa
<br>@Temperature -55.0 °C
 103000 psi
<br>@Temperature -67.0 °F
 90°, Dry
765 MPa
<br>@Temperature -55.0 °C
 111000 psi
<br>@Temperature -67.0 °F
 0°, Dry
765 MPa
<br>@Temperature 93.3 °C
 111000 psi
<br>@Temperature 200 °F
 90°, Dry
793 MPa
<br>@Temperature 25.0 °C
 115000 psi
<br>@Temperature 77.0 °F
 90°, Dry
800 MPa
<br>@Temperature 90.6 °C
 116000 psi
<br>@Temperature 195 °F
 0°, Dry
827 MPa
<br>@Temperature 25.0 °C
 120000 psi
<br>@Temperature 77.0 °F
 0°, Dry
Tensile Modulus 65.5 GPa
<br>@Temperature -67.0 °C
 9500 ksi
<br>@Temperature -88.6 °F
 0°, Dry
65.5 GPa
<br>@Temperature 77.0 °C
 9500 ksi
<br>@Temperature 171 °F
 90°, Dry
66.2 GPa
<br>@Temperature 195 °C
 9600 ksi
<br>@Temperature 383 °F
 0°, Dry
66.2 GPa
<br>@Temperature -67.0 °C
 9600 ksi
<br>@Temperature -88.6 °F
 90°, Dry
67.6 GPa
<br>@Temperature 77.0 °C
 9800 ksi
<br>@Temperature 171 °F
 0°, Dry
67.6 GPa
<br>@Temperature 200 °C
 9800 ksi
<br>@Temperature 392 °F
 90°, Dry
Compressive Yield Strength 586 MPa
<br>@Temperature 90.6 °C
 85000 psi
<br>@Temperature 195 °F
 0°, Wet
600 MPa
<br>@Temperature 90.6 °C
 87000 psi
<br>@Temperature 195 °F
 0°, Wet, Fill Compression
696 MPa
<br>@Temperature 71.1 °C
 101000 psi
<br>@Temperature 160 °F
 0°, Wet, Fill Compression
703 MPa
<br>@Temperature 71.1 °C
 102000 psi
<br>@Temperature 160 °F
 0°, Wet
758 MPa
<br>@Temperature 90.6 °C
 110000 psi
<br>@Temperature 195 °F
 0°, Dry
786 MPa
<br>@Temperature 90.6 °C
 114000 psi
<br>@Temperature 195 °F
 0°, Dry, Fill Compression
800 MPa
<br>@Temperature 25.0 °C
 116000 psi
<br>@Temperature 77.0 °F
 0°, Wet, Fill Compression
876 MPa
<br>@Temperature -55.0 °C
 127000 psi
<br>@Temperature -67.0 °F
 0°, Dry, Fill Compression
876 MPa
<br>@Temperature 25.0 °C
 127000 psi
<br>@Temperature 77.0 °F
 0°, Dry, Fill Compression
883 MPa
<br>@Temperature 25.0 °C
 128000 psi
<br>@Temperature 77.0 °F
 0°, Dry
958 MPa
<br>@Temperature -55.0 °C
 139000 psi
<br>@Temperature -67.0 °F
 0°, Dry
Compressive Modulus 59.3 GPa
<br>@Temperature 71.1 °C
 8600 ksi
<br>@Temperature 160 °F
 0°, Wet
60.0 GPa
<br>@Temperature -55.0 °C
 8700 ksi
<br>@Temperature -67.0 °F
 0°, Dry
60.0 GPa
<br>@Temperature 25.0 °C
 8700 ksi
<br>@Temperature 77.0 °F
 0°, Dry
60.7 GPa
<br>@Temperature 90.6 °C
 8800 ksi
<br>@Temperature 195 °F
 0°, Dry
Shear Strength 58.6 MPa
<br>@Temperature 90.6 °C
 8500 psi
<br>@Temperature 195 °F
 0° Short Beam, Wet
58.6 MPa
<br>@Temperature 90.6 °C
 8500 psi
<br>@Temperature 195 °F
 Fill Short Beam, Wet
70.3 MPa
<br>@Temperature 90.6 °C
 10200 psi
<br>@Temperature 195 °F
 0° Short Beam, Dry
70.3 MPa
<br>@Temperature 90.6 °C
 10200 psi
<br>@Temperature 195 °F
 Fill Short Beam, Dry
71.7 MPa
<br>@Temperature 71.1 °C
 10400 psi
<br>@Temperature 160 °F
 0° Short Beam, Wet
74.5 MPa
<br>@Temperature -55.0 °C
 10800 psi
<br>@Temperature -67.0 °F
 Fill Short Beam, Dry
75.2 MPa
<br>@Temperature 25.0 °C
 10900 psi
<br>@Temperature 77.0 °F
 0° Short Beam, Wet
78.6 MPa
<br>@Temperature 25.0 °C
 11400 psi
<br>@Temperature 77.0 °F
 Fill Short Beam, Wet
81.4 MPa
<br>@Temperature 25.0 °C
 11800 psi
<br>@Temperature 77.0 °F
 Fill Short Beam, Dry
84.1 MPa
<br>@Temperature 25.0 °C
 12200 psi
<br>@Temperature 77.0 °F
 0° Short Beam, Dry
101 MPa
<br>@Temperature -55.0 °C
 14600 psi
<br>@Temperature -67.0 °F
 0° Short Beam, Dry
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 121 °C
250 °F
Epoxy Matrix Limit