Haynes 75 Nickel Alloy Sheet, Annealed at 1925°F (1050°C)

Category Metal , Nonferrous Metal , Nickel Alloy
Manufacturer Haynes International, Inc.
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Haynes 75 Nickel Alloy Sheet, Annealed at 1925°F (1050°C).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Haynes alloy 75 is a solution-strengthened nickel-chromium alloy with moderate strength to 1200°F (650°C). It is principally used in low stress elevated temperature applications requiring reasonable oxidation resistance, and is approximately equivalent to alloy 600 in performance. Alloy 75 is used in a number of fabricated part applications in the gas turbine and aerospace industries in Europe, and is also employed in general industrial heating uses. The alloy is readily formed and fabricated using conventional techniques.Data provided by the manufacturer, Haynes International, Inc.
Physical Properties Metric English Comments
Density 8.37 g/cc
0.302 lb/in³
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 66.0 MPa

@Temperature 980 °C
 9570 psi

@Temperature 1800 °F
286 MPa

@Temperature 760 °C
 41500 psi

@Temperature 1400 °F
439 MPa

@Temperature 870 °C
 63700 psi

@Temperature 1600 °F
473 MPa

@Temperature 650 °C
 68600 psi

@Temperature 1200 °F
726 MPa

@Temperature 540 °C
 105000 psi

@Temperature 1000 °F
792 MPa

@Temperature 25.0 °C
 115000 psi

@Temperature 77.0 °F
Tensile Strength, Yield 31.0 MPa

@Strain 0.200 %,
Temperature 980 °C
 4500 psi

@Strain 0.200 %,
Temperature 1800 °F
68.0 MPa

@Strain 0.200 %,
Temperature 870 °C
 9860 psi

@Strain 0.200 %,
Temperature 1600 °F
152 MPa

@Strain 0.200 %,
Temperature 760 °C
 22000 psi

@Strain 0.200 %,
Temperature 1400 °F
275 MPa

@Strain 0.200 %,
Temperature 650 °C
 39900 psi

@Strain 0.200 %,
Temperature 1200 °F
363 MPa

@Strain 0.200 %,
Temperature 540 °C
 52600 psi

@Strain 0.200 %,
Temperature 1000 °F
407 MPa

@Strain 0.200 %,
Temperature 25.0 °C
 59000 psi

@Strain 0.200 %,
Temperature 77.0 °F
Elongation at Break 27 %

@Temperature 540 °C
 27 %

@Temperature 1000 °F
 2-inch (51 mm) sample
31 %

@Temperature 25.0 °C
 31 %

@Temperature 77.0 °F
 2-inch (51 mm) sample
32 %

@Temperature 650 °C
 32 %

@Temperature 1200 °F
 2-inch (51 mm) sample
75 %

@Temperature 760 °C
 75 %

@Temperature 1400 °F
 2-inch (51 mm) sample
90 %

@Temperature 870 °C
 90 %

@Temperature 1600 °F
 2-inch (51 mm) sample
91 %

@Temperature 980 °C
 91 %

@Temperature 1800 °F
 2-inch (51 mm) sample
Rupture Strength 8.30 MPa

@Temperature 870 °C,
Time 3.60e+6 sec
 1200 psi

@Temperature 1600 °F,
Time 1000 hour
 Typical Stress-Rupture
14.0 MPa

@Temperature 870 °C,
Time 360000 sec
 2030 psi

@Temperature 1600 °F,
Time 100 hour
 Typical Stress-Rupture
15.0 MPa

@Temperature 815 °C,
Time 3.60e+6 sec
 2180 psi

@Temperature 1500 °F,
Time 1000 hour
 Typical Stress-Rupture
25.0 MPa

@Temperature 870 °C,
Time 36000 sec
 3630 psi

@Temperature 1600 °F,
Time 10.0 hour
 Typical Stress-Rupture
26.0 MPa

@Temperature 815 °C,
Time 360000 sec
 3770 psi

@Temperature 1500 °F,
Time 100 hour
 Typical Stress-Rupture
26.0 MPa

@Temperature 760 °C,
Time 3.60e+6 sec
 3770 psi

@Temperature 1400 °F,
Time 1000 hour
 Typical Stress-Rupture
40.0 MPa

@Temperature 815 °C,
Time 36000 sec
 5800 psi

@Temperature 1500 °F,
Time 10.0 hour
 Typical Stress-Rupture
41.0 MPa

@Temperature 760 °C,
Time 360000 sec
 5950 psi

@Temperature 1400 °F,
Time 100 hour
 Typical Stress-Rupture
47.0 MPa

@Temperature 705 °C,
Time 3.60e+6 sec
 6820 psi

@Temperature 1300 °F,
Time 1000 hour
 Typical Stress-Rupture
66.0 MPa

@Temperature 760 °C,
Time 36000 sec
 9570 psi

@Temperature 1400 °F,
Time 10.0 hour
 Typical Stress-Rupture
70.0 MPa

@Temperature 705 °C,
Time 360000 sec
 10200 psi

@Temperature 1300 °F,
Time 100 hour
 Typical Stress-Rupture
83.0 MPa

@Temperature 650 °C,
Time 3.60e+6 sec
 12000 psi

@Temperature 1200 °F,
Time 1000 hour
 Typical Stress-Rupture
110 MPa

@Temperature 705 °C,
Time 36000 sec
 16000 psi

@Temperature 1300 °F,
Time 10.0 hour
 Typical Stress-Rupture
130 MPa

@Temperature 650 °C,
Time 360000 sec
 18900 psi

@Temperature 1200 °F,
Time 100 hour
 Typical Stress-Rupture
185 MPa

@Temperature 650 °C,
Time 36000 sec
 26800 psi

@Temperature 1200 °F,
Time 10.0 hour
 Typical Stress-Rupture
Modulus of Elasticity 140 GPa

@Temperature 1000 °C
 20300 ksi

@Temperature 1830 °F
 Dynamic
153 GPa

@Temperature 900 °C
 22200 ksi

@Temperature 1650 °F
 Dynamic
165 GPa

@Temperature 800 °C
 23900 ksi

@Temperature 1470 °F
 Dynamic
173 GPa

@Temperature 700 °C
 25100 ksi

@Temperature 1290 °F
 Dynamic
181 GPa

@Temperature 600 °C
 26300 ksi

@Temperature 1110 °F
 Dynamic
197 GPa

@Temperature 400 °C
 28600 ksi

@Temperature 752 °F
 Dynamic
210 GPa

@Temperature 200 °C
 30500 ksi

@Temperature 392 °F
 Dynamic
221 GPa

@Temperature 20.0 °C
 32100 ksi

@Temperature 68.0 °F
 Dynamic
Thermal Properties Metric English Comments
CTE, linear 14.3 µm/m-°C

@Temperature 20.0 - 500 °C
 7.94 µin/in-°F

@Temperature 68.0 - 932 °F
15.0 µm/m-°C

@Temperature 20.0 - 600 °C
 8.33 µin/in-°F

@Temperature 68.0 - 1110 °F
15.4 µm/m-°C

@Temperature 20.0 - 700 °C
 8.56 µin/in-°F

@Temperature 68.0 - 1290 °F
16.5 µm/m-°C

@Temperature 20.0 - 800 °C
 9.17 µin/in-°F

@Temperature 68.0 - 1470 °F
17.1 µm/m-°C

@Temperature 20.0 - 900 °C
 9.50 µin/in-°F

@Temperature 68.0 - 1650 °F
18.2 µm/m-°C

@Temperature 20.0 - 1000 °C
 10.1 µin/in-°F

@Temperature 68.0 - 1830 °F
Thermal Conductivity 18.6 W/m-K

@Temperature 400 °C
 129 BTU-in/hr-ft²-°F

@Temperature 752 °F
22.7 W/m-K

@Temperature 600 °C
 158 BTU-in/hr-ft²-°F

@Temperature 1110 °F
24.7 W/m-K

@Temperature 700 °C
 171 BTU-in/hr-ft²-°F

@Temperature 1290 °F
26.5 W/m-K

@Temperature 800 °C
 184 BTU-in/hr-ft²-°F

@Temperature 1470 °F
28.4 W/m-K

@Temperature 900 °C
 197 BTU-in/hr-ft²-°F

@Temperature 1650 °F
30.1 W/m-K

@Temperature 1000 °C
 209 BTU-in/hr-ft²-°F

@Temperature 1830 °F
Melting Point 1340 - 1380 °C
2440 - 2520 °F
Solidus 1340 °C
2440 °F
Liquidus 1380 °C
2520 °F
Electrical Properties Metric English Comments
Electrical Resistivity 0.000112 ohm-cm

@Temperature 200 °C
 0.000112 ohm-cm

@Temperature 392 °F
0.000115 ohm-cm

@Temperature 600 °C
 0.000115 ohm-cm

@Temperature 1110 °F
0.000115 ohm-cm

@Temperature 700 °C
 0.000115 ohm-cm

@Temperature 1290 °F
0.000115 ohm-cm

@Temperature 800 °C
 0.000115 ohm-cm

@Temperature 1470 °F
0.000115 ohm-cm

@Temperature 900 °C
 0.000115 ohm-cm

@Temperature 1650 °F
0.000116 ohm-cm

@Temperature 1000 °C
 0.000116 ohm-cm

@Temperature 1830 °F
0.000117 ohm-cm

@Temperature 400 °C
 0.000117 ohm-cm

@Temperature 752 °F
Processing Properties Metric English Comments
Annealing Temperature 1052 °C