H.C. Starck Amperit® 588.059 Chromium Carbide-Nickel Chromium 75-25 (Cr3C2-NiCr)
| Category | Ceramic , Carbide |
| Manufacturer | H.C. Starck |
| Trade Name | Amperit® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | H.C. Starck Amperit® 588.059 Chromium Carbide-Nickel Chromium 75-25 (Cr3C2-NiCr).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 2.50 - 3.20 g/cc | 0.0903 - 0.116 lb/in³ | ASTM B417 |
| Particle Size | 9.0 - 13 µm | 9.0 - 13 µm | 10% |
| 18 - 24 µm | 18 - 24 µm | 50% | |
| 30 - 40 µm | 30 - 40 µm | 90% | |
| 62 µm | 62 µm | minimum 99.5% | |
| 88 µm | 88 µm | 100% less than |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Carbon, C | 9.0 - 11 % | 9.0 - 11 % | |
| Chromium, Cr | 65.9 - 73 % | 65.9 - 73 % | |
| Iron, Fe | <= 0.50 % | <= 0.50 % | |
| Nickel, Ni | 18 - 22 % | 18 - 22 % | |
| Oxygen, O | <= 0.60 % | <= 0.60 % |
Users viewing this material also viewed the following:
- Network Polymers MS 100 Styrene Methyl Methacrylate Copolymer
- DuPont™ Dartek® F-101 Nylon 6,6 Forming Film, 25 µm Thickness (discontinued **)
- Saint-Gobain Rulon® 1337 Bearing/Seal PTFE
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane, 350ºF Cure Temperature
- TIMET 6-4 Titanium Alloy (Ti-6Al-4V; ASTM Grade 5) Sheet
- Hexcel® UHM Carbon Fiber (3000 Filaments)
- Chosun Refractories HSC-16SF-W2 Dense and High-Strength Castable, Credens
- CIMBAR BARA 200 Barium Sulfate (BaSO4)
- Bisalloy Steels BisPlate 60 Thickness 16-80 mm
Copyright © lookpolymers.com All Rights Reserved