H.C. Starck 3403 Molybdenum Alloy APT-3 TZM, Arc-Cast Plate

Category Metal , Nonferrous Metal , Molybdenum Alloy
Manufacturer H.C. Starck
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF H.C. Starck 3403 Molybdenum Alloy APT-3 TZM, Arc-Cast Plate.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Arc-Cast Plate 3403Description of Product: This specification covers rolled plate of carbon-deoxidized TZM alloy (molybdenum + 0.5% titanium + 0.08% zirconium) produced from sheet bar consolidated by the H.C. Stark consumable electrode vacuum-arc-casting process.Structure: Plate will be supplied in a stress-relieved condition unless otherwise requested.Information provided by H.C. Starck.
Mechanical Properties Metric English Comments
Tensile Strength >= 689 MPa

@Thickness 25.4 - 38.1 mm
>= 100000 psi

@Thickness 1.00 - 1.50 in
ASTM E-8
>= 758 MPa

@Thickness 12.7 - 25.4 mm
>= 110000 psi

@Thickness 0.500 - 1.00 in
ASTM E-8
>= 827 MPa

@Thickness 4.762 - 12.7 mm
>= 120000 psi

@Thickness 0.1875 - 0.500 in
ASTM E-8
Tensile Strength, Yield >= 586 MPa

@Strain 0.200 %,
Thickness 25.4 - 38.1 mm
>= 85000 psi

@Strain 0.200 %,
Thickness 1.00 - 1.50 in
ASTM E-8
>= 655 MPa

@Strain 0.200 %,
Thickness 12.7 - 25.4 mm
>= 95000 psi

@Strain 0.200 %,
Thickness 0.500 - 1.00 in
ASTM E-8
>= 689 MPa

@Strain 0.200 %,
Thickness 4.762 - 12.7 mm
>= 100000 psi

@Strain 0.200 %,
Thickness 0.1875 - 0.500 in
ASTM E-8
Elongation at Break >= 8.0 %

@Thickness 25.4 - 38.1 mm
>= 8.0 %

@Thickness 1.00 - 1.50 in
ASTM E-8
>= 10 %

@Thickness 4.762 - 12.7 mm
>= 10 %

@Thickness 0.1875 - 0.500 in
ASTM E-8
>= 10 %

@Thickness 12.7 - 25.4 mm
>= 10 %

@Thickness 0.500 - 1.00 in
ASTM E-8
Component Elements Properties Metric English Comments
Carbon, C 0.010 - 0.030 %
0.010 - 0.030 %
Iron, Fe <= 0.010 %
<= 0.010 %
Molybdenum, Mo >= 99.25 %
>= 99.25 %
by difference
Nickel, Ni <= 0.0020 %
<= 0.0020 %
Nitrogen, N <= 0.0020 %
<= 0.0020 %
Oxygen, O <= 0.0030 %
<= 0.0030 %
Silicon, Si <= 0.010 %
<= 0.010 %
Titanium, Ti 0.40 - 0.55 %
0.40 - 0.55 %
Zirconium, Zr 0.060 - 0.12 %
0.060 - 0.12 %