- Grupo Repol Dinalon® B1S25 G30 PA6 30% Glass Fiber
Grupo Repol Dinalon® B1S25 G30 PA6 30% Glass Fiber
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled |
| Manufacturer | Grupo Repol |
| Trade Name | Dinalon® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Grupo Repol Dinalon® B1S25 G30 PA6 30% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Mechanical properties for Dry As Molded samplesInformation provided by Grupo Repol
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.36 g/cc | 0.0491 lb/in³ | ISO 1183/A |
| Moisture Absorption at Equilibrium | <= 0.25 % | <= 0.25 % | Karl-Fischer; ISO 15512/A |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 190 MPa | 27600 psi | ISO 527 |
| Elongation at Break | 3.5 % | 3.5 % | ISO 527 |
| Tensile Modulus | 9.00 GPa | 1310 ksi | ISO 527 |
| Flexural Strength | 230 MPa | 33400 psi | ISO 178 |
| Flexural Modulus | 6.40 GPa | 928 ksi | ISO 178 |
| Charpy Impact Unnotched | 5.20 J/cm² @Temperature 23.0 °C |
24.7 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU |
| Charpy Impact, Notched | 1.30 J/cm² @Temperature 23.0 °C |
6.19 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | ISO 75/A |
| Vicat Softening Point | >= 200 °C | >= 392 °F | 50N; ISO 306 |
Users viewing this material also viewed the following:
- Multibase SILASTIC® C7-4550 CADOX TS-50S Dow-Corning Biomedical Grade ETR Elastomer
- MV Labs NI750 {Ni(NH3)6}(NO3)2 Hexaminenickel(II) nitrate
- PolyOne Bergamid™ A700 G20 U-SO Polyamide 66 (Nylon 66)
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with Cumar P-10 Plasticizer
- Ensinger Tecatron® XP-61 Compression Molded PPS Compound, 25% Fiberglass and Mineral Filled
- Diamond Polymers ABS 3500ELG
- E-Polymers EFLEX® V2060 SEBS/TPV
- Albis Plastics Cellulose Acetate Butyrate B9004 (Odor Mask Added), 10% Plasticizer (discontinued **)
- ChevronTexaco Ulti-Plex® NLGI 2 Greases EP
- A. Schulman POLYFLAM™ E-13030B Reinforced Super Coupled Polypropylene Black
Copyright © lookpolymers.com All Rights Reserved