Gromax CFG45-PN11N1 Nylon 6 46% Glass Filled (Dry)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 50% Glass Fiber Filled |
| Manufacturer | Gromax |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Gromax CFG45-PN11N1 Nylon 6 46% Glass Filled (Dry).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Gromax Enterprises Corp.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.60 g/cc | 1.60 g/cc | ISO 1183 |
| Moisture Absorption | 0.760 % | 0.760 % | ISO 62 |
| Maximum Moisture Content | 0.10 | 0.10 | Karl Fischer |
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm @Temperature 80.0 °C |
0.0020 in/in @Temperature 176 °F |
60x60x2 mm; ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0060 cm/cm @Temperature 80.0 °C |
0.0060 in/in @Temperature 176 °F |
60x60x2 mm; ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 90 | 90 | [N/mm<sup>2<sup>]; ISO 7619 |
| Tensile Strength | 193 MPa | 28000 psi | 50 mm/min; ISO 527 |
| Elongation at Break | 3.3 % | 3.3 % | 50 mm/min; ISO 527 |
| Flexural Strength | 296 MPa | 42900 psi | 5 mm/min; ISO 178 |
| Flexural Modulus | 11.6 GPa | 1680 ksi | 5 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 17.6 kJ/m² | 8.37 ft-lb/in² | ISO 180-1A |
| Charpy Impact Unnotched | 9.30 J/cm² @Temperature 23.0 °C |
44.3 ft-lb/in² @Temperature 73.4 °F |
ISO 179-1eU |
| Charpy Impact, Notched | 1.80 J/cm² @Temperature 23.0 °C |
8.57 ft-lb/in² @Temperature 73.4 °F |
ISO 179-1A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 236 °C | 457 °F | ISO 75-1,-2 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 266 - 280 °C | 511 - 536 °F | ISO 294 |
| Mold Temperature | 80.0 - 120 °C | 176 - 248 °F | ISO 294 |
| Drying Temperature | 80.0 °C | 176 °F | |
| Dry Time | 2.00 - 6.00 hour | 2.00 - 6.00 hour |
Users viewing this material also viewed the following:
- DuPont Performance Polymers Hypalon® 45 Chlorosulfonated Polyethylene Rubber, Peroxide Cured Carbon Black Filled Compound
- Lehmann & Voss LUVOCOM® 1105/BK7308 PEEK, unreinforced
- Master Bond Supreme 3HT-80 One Component, Toughened, Heat Curing Epoxy
- Addcomp ADD-VANCE® THC 453 PP based masterbatch containing heat stabilizers and carbon black
- Adell BT-37 Nylon 6, 35% Glass Reinforced; Impact Modified
- Carpenter MP35N* Ni-Co-Cr-Mo Alloy, 35% Cold Reduction + Aged 538°C (1000°F)/4hr/AC
- BASF Heligoen® Blue L 7072 D Color Additive
- Beijing Ranger Chem PBT-201-G15 202 Environmental Protection Flame Retarding FR PBT
- Fainplast Compounds PM 8220 Flexible PVC, Lead Free
- Karina E 08/415-FC-LMP Beige Color Concentrate for PVC
Copyright © lookpolymers.com All Rights Reserved