- Gromax CCP ABS/PBT 7320H-104 20% Glass Fiber Filled
Gromax CCP ABS/PBT 7320H-104 20% Glass Fiber Filled
| Category | Polymer , Thermoplastic , ASA Polymer , Polyester, TP , Polybutylene Terephthalate (PBT) , PBT + ASA Blend, Glass Fiber Reinforced |
| Manufacturer | Gromax |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Gromax CCP ABS/PBT 7320H-104 20% Glass Fiber Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Product Description: A 20% glass fiber reinforced injection molding grade. Characteristics:Low warp age and excellent dimensionally stable Excellent electrical property Excellent mechanic and chemical property Excellent weatherability Excellent wear property Excellent moldability High resistance to fuels, oil, fats and many solventsInformation provided by Gromax Enterprises Corp.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.34 g/cc | 1.34 g/cc | ASTM D792 |
| Moisture Absorption | 0.0400 % @Time 86400 sec |
0.0400 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage | 0.0010 - 0.0040 cm/cm @Thickness 1.60 mm |
0.0010 - 0.0040 in/in @Thickness 0.0630 in |
horizontal; ASTM D955 |
| 0.0070 - 0.013 cm/cm @Thickness 1.60 mm |
0.0070 - 0.013 in/in @Thickness 0.0630 in |
vertical; ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 83.4 MPa | 12100 psi | ASTM D638 |
| Elongation at Break | 3.5 % | 3.5 % | ASTM D638 |
| Flexural Strength | 120 MPa | 17400 psi | ASTM D790 |
| Flexural Modulus | 4.90 GPa | 711 ksi | ASTM D790 |
| Izod Impact, Notched | >= 0.834 J/cm @Thickness 6.35 mm |
>= 1.56 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 30.0 µm/m-°C | 16.7 µin/in-°F | ASTM D696 |
| Melting Point | 225 °C | 437 °F | DSC |
| Deflection Temperature at 1.8 MPa (264 psi) | 150 °C | 302 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | ASTM D257 |
| Dielectric Strength | 20.0 kV/mm @Thickness 2.00 mm |
508 kV/in @Thickness 0.0787 in |
ASTM D149 |
| Arc Resistance | 80 sec | 80 sec | ASTM D495 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 240 - 270 °C | 464 - 518 °F | |
| Nozzle Temperature | 250 - 270 °C | 482 - 518 °F | |
| Mold Temperature | 40.0 - 120 °C | 104 - 248 °F | suitable temperature 60-80°C |
| Injection Pressure | 50.0 - 120 MPa | 7250 - 17400 psi | |
| Hold Pressure | 30.0 - 80.0 MPa | 4350 - 11600 psi | |
| Back Pressure | 0.000 - 0.300 MPa | 0.000 - 43.5 psi | |
| Screw Speed | 60 - 120 rpm | 60 - 120 rpm | to be chosen in such a way that plasticizing time is just within cooling time |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Injection Rate | middle-fast |
Users viewing this material also viewed the following:
- Nye Lubricants UniFlor 8960 (498A) (UF) Synthetic Oil
- Nanocyl NANOCYL™ NC2101 Double-Wall Isolated and Bundled Carbon Nanotubes - Research Grade
- Pasargad Polymer Peyvand Pasamid 3P-H1000W Nylon 6
- PolyMirae Moplen EP300R Injection Molding Grade Polypropylene
- Master Bond EP30HT-LO NASA Low Outgassing, Optically Clear Coating
- Unipetrol C4 Fraction
- Cheng Yu Plastic NG1200S Nylon 66, 20% Glass Fiber Reinforced
- ConocoPhillips SynXPA® H-500 H Lubricant H-500
- Barlog Plastics KEBATER BF115 PBT, 15% glass fiber reinforced
Copyright © lookpolymers.com All Rights Reserved