Gouda Vuurvast VIBRON 160 H GS (R) Dense Vibrating Refractory Castable
| Category | Ceramic , Oxide , Aluminum Oxide , Silicon Oxide |
| Manufacturer | Gouda Vuurvast |
| Trade Name | VIBRON |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Gouda Vuurvast VIBRON 160 H GS (R) Dense Vibrating Refractory Castable.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Vibron 160 H GS (R) is a pumpable low cement castable based on high fired high alumina grog and characterized by a high strength and good thermal shock-, corrosion- and abrasion resistance. Because of special additives, this low cement castable is special suited for a faster heating schedule.Remarks: Indicated values apply to vibrated products.Information provided by Gouda Vuurvast.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 2.55 - 2.65 g/cc | 0.0921 - 0.0957 lb/in³ | After drying at 110°C |
| Particle Size | <= 6000 µm | <= 6000 µm | Grain Size |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Compressive Strength | 75.0 - 85.0 MPa @Temperature 100 °C |
10900 - 12300 psi @Temperature 212 °F |
Cold Crushing Strength |
| 90.0 - 110 MPa @Temperature 1400 °C |
13100 - 16000 psi @Temperature 2550 °F |
Cold Crushing Strength |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 1.33 - 1.43 W/m-K @Temperature 100 °C |
9.23 - 9.92 BTU-in/hr-ft²-°F @Temperature 212 °F |
|
| 1.35 - 1.45 W/m-K @Temperature 600 °C |
9.37 - 10.1 BTU-in/hr-ft²-°F @Temperature 1110 °F |
||
| 1.45 - 1.55 W/m-K @Temperature 1400 °C |
10.1 - 10.8 BTU-in/hr-ft²-°F @Temperature 2550 °F |
||
| Maximum Service Temperature, Air | 1600 °C | 2910 °F | |
| Shrinkage | -0.400 - 0.400 % @Temperature 1400 °C |
-0.400 - 0.400 % @Temperature 2550 °F |
Permanent Linear Change |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Al2O3 | 61 % | 61 % | |
| Fe2O3 | 1.0 % | 1.0 % | |
| SiO2 | 35 % | 35 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Material Consumption per 1 m3 | 2550 kg | |
| Mixing Water | 5-6 liters | per 100 kgs dry material |
Users viewing this material also viewed the following:
- Polykemi AB POLYfill PPH T20020 UV Polypropylene Homopolymer, Mineral Reinforced, UV-Stabilized
- LG Chemical MP211 ABS, Low Gloss, Metal Plating
- Lubriplate 72-C Oil Food Machinery Oil
- Samsung Cheil Industries Starex® HR-0370F ABS, Unreinforced Heat Resistant
- Schott N-LAK10 Glass
- SABIC Innovative Plastics Xenoy® X4850 PBT+PC (Asia Pacific)
- Toyobo VYLOPET® CA3300 PC/PBT Polymer Alloy, Impact Resistant, Chemical Resistant
- Braskem RP 347 Injection Molding Polypropylene
- 3M Dyneon™ ET 6210AZ Fluoroplastic Agglomerate
- Samsung Cheil Industries Infino® CF-1030 PC, Unreinforced High Impact
Copyright © lookpolymers.com All Rights Reserved