Fujipoly Industries Sarcon® 85H Thin-Film HR

Category Polymer , Thermoset , Silicone
Manufacturer Fujipoly Industries
Trade Name Sarcon®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Fujipoly Industries Sarcon® 85H Thin-Film HR.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Sarcon HR is Fujipolys originally developed High Heat Conductive Silicone Rubber. Fine, high heat conductive ceramic particles are mixed with insulative silicone rubber.Sarcon GHR is a composite of Heat Conductive Silicone Rubber and fiberglass.Information provided by Fujipoly Industries
Mechanical Properties Metric English Comments
Hardness, Shore A 85
85
ASTM D2240
86
86
60°C for 500 hrs; ASTM D2240
94
94
150°C for 1,000 hrs; ASTM D2240
95
95
200°C for 1,000 hrs; ASTM D2240
Tensile Strength, Yield 4.941 MPa
716.6 psi
5.647 MPa
819.0 psi
150°C for 1,000 hrs
5.882 MPa
853.1 psi
200°C for 1,000 hrs
Elongation at Yield 25 %
25 %
200°C for 1,000 hrs
30 %
30 %
150°C for 1,000 hrs
60 %
60 %
Tear Strength 0.600 kN/m
3.42 pli
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 182 °C
360 °F
Minimum Service Temperature, Air -60.0 °C
-76.0 °F
Flammability, UL94 V-0
V-0
Electrical Properties Metric English Comments
Volume Resistivity 2.60e+13 ohm-cm
2.60e+13 ohm-cm
60°C for 500 hrs
1.00e+15 ohm-cm
1.00e+15 ohm-cm
7.60e+15 ohm-cm
7.60e+15 ohm-cm
200°C for 1,000 hrs
7.70e+15 ohm-cm
7.70e+15 ohm-cm
150°C for 1,000 hrs
Dielectric Constant 5.4

@Frequency 50 Hz
 5.4

@Frequency 50 Hz
5.4

@Frequency 1000 Hz
 5.4

@Frequency 1000 Hz
 After 1000 hrs at 200°C
5.4

@Frequency 1e+6 Hz
 5.4

@Frequency 1e+6 Hz
5.4

@Frequency 1e+6 Hz
 5.4

@Frequency 1e+6 Hz
 After 1000 hrs at 200°C
5.5

@Frequency 1000 Hz
 5.5

@Frequency 1000 Hz
 After 1000 hrs at 150°C
5.5

@Frequency 1e+6 Hz
 5.5

@Frequency 1e+6 Hz
 After 1000 hrs at 150°C
5.5

@Frequency 50 Hz
 5.5

@Frequency 50 Hz
 After 1000 hrs at 150°C
5.5

@Frequency 50 Hz
 5.5

@Frequency 50 Hz
 After 1000 hrs at 200°C
5.7

@Frequency 1000 Hz
 5.7

@Frequency 1000 Hz
6.0

@Frequency 1000 Hz
 6.0

@Frequency 1000 Hz
 After 500 hrs at 60°C
6.0

@Frequency 1e+6 Hz
 6.0

@Frequency 1e+6 Hz
 After 500 hrs at 60°C
6.4

@Frequency 50 Hz
 6.4

@Frequency 50 Hz
 After 500 hrs at 60°C
Dielectric Strength 6.00 kV/mm
152 kV/in
60°C for 500 hrs
11.5 kV/mm
292 kV/in
AC 60 Hz; 150°C for 1,000 hrs
12.4 kV/mm
315 kV/in
200°C for 1,000 hrs
14.0 kV/mm
356 kV/in
AC 60 Hz
Dielectric Breakdown 10000 V
10000 V
Withstand Voltage [V/min]; AC 60 Hz
Dissipation Factor 0.0020

@Frequency 1000 Hz
 0.0020

@Frequency 1000 Hz
 After 1000 hrs at 150°C
0.0020

@Frequency 50 Hz
 0.0020

@Frequency 50 Hz
 After 1000 hrs at 200°C
0.0020

@Frequency 1000 Hz
 0.0020

@Frequency 1000 Hz
 After 1000 hrs at 200°C
0.0020

@Frequency 1e+6 Hz
 0.0020

@Frequency 1e+6 Hz
 After 1000 hrs at 200°C
0.0020

@Frequency 1000 Hz
 0.0020

@Frequency 1000 Hz
0.0020

@Frequency 1e+6 Hz
 0.0020

@Frequency 1e+6 Hz
0.0030

@Frequency 1e+6 Hz
 0.0030

@Frequency 1e+6 Hz
 After 1000 hrs at 150°C
0.0030

@Frequency 50 Hz
 0.0030

@Frequency 50 Hz
 After 1000 hrs at 150°C
0.0040

@Frequency 50 Hz
 0.0040

@Frequency 50 Hz
0.0070

@Frequency 1e+6 Hz
 0.0070

@Frequency 1e+6 Hz
 After 500 hrs at 60°C
0.013

@Frequency 1000 Hz
 0.013

@Frequency 1000 Hz
 After 500 hrs at 60°C
0.023

@Frequency 50 Hz
 0.023

@Frequency 50 Hz
 After 500 hrs at 60°C
Descriptive Properties Value Comments
Color Brown
Thermal Impedance 0.76°C/W
FTM P-3010; ASTM D5470