Freudenberg Simrit S60 Silicone Elastomer (VMQ)
| Category | Polymer , Thermoset , Rubber or Thermoset Elastomer (TSE) , Silicone |
| Manufacturer | Freudenberg Simrit |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Freudenberg Simrit S60 Silicone Elastomer (VMQ).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
General Purpose; AMS 3301; A-A-59588 (ZZ-R-765) Class 2A, 2B Grade 40; Good heat resistance. Poor resistance to abrasion, tear and cut growth; low tensile strength; inferior resistance to oil, gasoline and solvents; poor resistance to alkalis and acids.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.22 g/cc | 1.22 g/cc | Original Properties; ASTM D297 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 60 | 60 | Original Properties; ASTM D2240 |
| 53 @Temperature 150 °C |
53 @Temperature 302 °F |
ASTM #1 Oil Immersion for 70 hours; ASTM D2240 | |
| 66 @Temperature 225 °C |
66 @Temperature 437 °F |
Air Aging, 70 hours; ASTM D2240 | |
| Tensile Strength, Ultimate | 6.55 MPa | 950 psi | Original Properties; ASTM D412 Die C |
| 5.830 MPa @Temperature 225 °C |
845.5 psi @Temperature 437 °F |
Air Aging, 70 hours; ASTM D412 Die C | |
| 6.03 MPa @Temperature 150 °C |
874 psi @Temperature 302 °F |
ASTM #1 Oil Immersion for 70 hours; ASTM D412 Die C | |
| Elongation at Break | 350 % | 350 % | Original Properties; ASTM D412 Die C |
| 248.5 % @Temperature 225 °C |
248.5 % @Temperature 437 °F |
Air Aging, 70 hours; ASTM D412 Die C | |
| 322 % @Temperature 150 °C |
322 % @Temperature 302 °F |
ASTM #1 Oil Immersion for 70 hours; ASTM D412 Die C | |
| Tear Strength | 17.9 kN/m | 102 pli | ASTM D624 Die B |
| Compression Set | 19 % @Temperature 150 °C, Time 252000 sec |
19 % @Temperature 302 °F, Time 70.0 hour |
25 max; ASTM D395 |
| 19 % @Temperature 150 °C, Time 252000 sec |
19 % @Temperature 302 °F, Time 70.0 hour |
40 max; ASTM D395 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Bend (flat) | Pass | Air Aging for 70 hours at 225°C |
| Color | Red | |
| Decomposition per AMS 3302G | None | |
| Low Temperature Brittleness | Pass, No cracks | ASTM D2137 |
| Surface Tackiness per AMS 3302G | None | |
| Volume Change (%), ASTM D471 | 2 | Water Immersion for 70 hours at 100°C |
| 6 | ASTM #1 Oil Immersion for 70 hours at 150°C |
Users viewing this material also viewed the following:
- Ravago Manufacturing Americas Hylac® GP55 ABS
- Karina 700D40/356-AT Green PVC Compound
- SGL Carbon Group SIGRAFIL C® C25 S003 EPY Staple Carbon Fiber, Epoxy Sizing
- Solvay Specialty Polymers Polidan® EC/MD Polyethylene, Crosslinked (XLPE)
- Techmer ES HiFill® TPX-PBT-01022 25% Mineral Filled
- Suqian Unitechem Antioxidant B215
- Cheng Yu Plastic ML1010 PC/PTFE
- Cosmic Plastics 6120F Short Glass Fiber Filled Ortho Diallyl Phthalate Molding Compound
- Plaslok 5314 Black (INJ) Impact Grade Phenolic Molding Compound (discontinued **)
Copyright © lookpolymers.com All Rights Reserved