Formosa Plastics Formolene® E927ND Film HDPE

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Film Grade
Manufacturer Formosa Plastics Corporation, USA
Trade Name Formolene®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Formosa Plastics Formolene® E927ND Film HDPE.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
High Molecular Weight High Density Polyethylene (HMW-HDPE) for Film Extrusion Formolene® E927ND is a bi-modal HMW-HDPE resin designed for high dart impact strength and good processing characteristics. Formolene® E927ND is well balanced in overall physical properties and provides good stiffness for thin gauge film applications. Formolene® E927ND meets all requirements of the U.S. Food and Drug Administration as specified in 21 CFR 177.1520, covering safe use of polyolefin articles intended for direct food contact.Applications: Industrial Liners, T-Shirt Bags, Trash Can Liner and Heavy Duty BagsInformation provided by Formosa Plastics Corporation, USA
Physical Properties Metric English Comments
Density 0.949 g/cc
0.0343 lb/in³
ASTM D1505
Thickness 15.2 microns
0.600 mil
Melt Flow 0.070 g/10 min

@Load 2.16 kg,
Temperature 190 °C
0.070 g/10 min

@Load 4.76 lb,
Temperature 374 °F
Condition E; ASTM D1238
High Load Melt Index 12 g/10 min

@Load 21.6 kg,
Temperature 190 °C
12 g/10 min

@Load 47.6 lb,
Temperature 374 °F
Condition F; ASTM D1238
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 445 %
445 %
ASTM D882
Film Elongation at Break, TD 547 %
547 %
ASTM D882
Elmendorf Tear Strength MD 8.0 g
8.0 g
ASTM D1922
Elmendorf Tear Strength TD 79 g
79 g
ASTM D1922
Dart Drop Test 373 g
0.822 lb
ASTM D1709
Film Tensile Strength at Break, MD 58.43 MPa
8475 psi
ASTM D882
Film Tensile Strength at Break, TD 49.70 MPa
7208 psi
ASTM D882
1% Secant Modulus, MD 517 MPa
75000 psi
ASTM D882
1% Secant Modulus, TD 917 MPa
133000 psi
ASTM D882
Thermal Properties Metric English Comments
Melting Point 131 °C
268 °F
DSC
Processing Properties Metric English Comments
Blow-up Ratio (BUR) 4.0
4.0