TSE Industries Millathane® 5004 Millable Polyurethane Elastomer with 40 PHR N330 (HAF) Black

Category	Polymer , Thermoset , Polyester, TS , Polyurethane, TS , Thermoset Polyurethane, Elastomer, Unreinforced , Rubber or Thermoset Elastomer (TSE)
Manufacturer	TSE Industries, Inc
Trade Name	Millathane®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	TSE Industries Millathane® 5004 Millable Polyurethane Elastomer with 40 PHR N330 (HAF) Black.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

MILLATHANE 5004 is a millable polyurethane elastomer having excellent processing characteristics. MILLATHANE 5004 stocks can be readily processed on conventional rubber equipment. Vulcanization is carried out by the use of various peroxides including dicumyl peroxide (DCP) or 2,5-dimethyl-2,5-bis (t-butylperoxy) hexane (DBPH).FormulationMillathane 5004100Stearic Acid0.25N330 (HAF) Black40Di-Cup 40C4.6All information provided by TSE Industries

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	75	75
	79	79	heat aged one week at 300ºF
	80	80	heat aged 70 hours at 300ºF
Tensile Strength, Yield	11.0 MPa	1600 psi	heat aged one week at 300ºF
	19.0 MPa	2760 psi	heat aged 70 hours at 300ºF
	28.5 MPa	4140 psi
Elongation at Yield	280 %	280 %	heat aged 70 hours at 300ºF
	310 %	310 %	heat aged one week at 300ºF
	340 %	340 %
100% Modulus	0.00427 GPa	0.620 ksi	heat aged one week at 300ºF
	0.00607 GPa	0.880 ksi	heat aged 70 hours at 300ºF
	0.00910 GPa	1.32 ksi
200% Modulus	0.00820 GPa	1.19 ksi	heat aged one week at 300ºF
	0.0137 GPa	1.99 ksi	heat aged 70 hours at 300ºF
	0.0196 GPa	2.84 ksi
300% Modulus	0.0110 GPa	1.59 ksi	heat aged one week at 300ºF
	0.0270 GPa	3.91 ksi

Processing Properties	Metric	English	Comments
Cure Time	30.0 min @Temperature 152 °C	0.500 hour @Temperature 305 °F