- Fiberfil® J-60/15/UV/HS Polypropylene Homopolymer, 15% Glass Reinforced, Heat Stabilized, UV Stabilized
Fiberfil® J-60/15/UV/HS Polypropylene Homopolymer, 15% Glass Reinforced, Heat Stabilized, UV Stabilized
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | FiberFil |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Fiberfil® J-60/15/UV/HS Polypropylene Homopolymer, 15% Glass Reinforced, Heat Stabilized, UV Stabilized.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by FIBERFIL Engineered Plastics
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.00 g/cc | 1.00 g/cc | ASTM D792 |
| Water Absorption | 0.030 % | 0.030 % | 24 hr; ASTM D570 |
| Linear Mold Shrinkage | 0.0040 - 0.0050 cm/cm @Thickness 3.17 mm |
0.0040 - 0.0050 in/in @Thickness 0.125 in |
ASTM D955 |
| 0.0050 - 0.0060 cm/cm @Thickness 6.35 mm |
0.0050 - 0.0060 in/in @Thickness 0.250 in |
ASTM D955 | |
| Melt Flow | 8.0 g/10 min | 8.0 g/10 min | 230/2.16 (typical); ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 100 - 110 | 100 - 110 | ASTM D785 |
| Tensile Strength, Yield | 62.1 MPa | 9000 psi | ASTM D638 |
| Elongation at Yield | 3.5 % | 3.5 % | ASTM D638 |
| Tensile Modulus | 2.76 GPa | 400 ksi | ASTM D638 |
| Flexural Strength | 65.0 MPa | 9430 psi | ASTM D790 |
| Flexural Modulus | 2.60 GPa | 377 ksi | Tangent; ASTM D790 |
| Izod Impact, Notched | 0.427 J/cm @Thickness 3.17 mm |
0.800 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 149 °C | 300 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 138 °C | 280 °F | ASTM D648 |
Users viewing this material also viewed the following:
- ICO Polymers ICOTEXâ„¢ 520-5004 1000 Micron EVA Powder
- Greene Tweed FPD Blueâ„¢ 707 Fluoroelastomer
- Taiwan PU Corporation TPUI-H85 High Hydrolysis Resistance, Injection Molding Polyether Base TPU
- Spartech Solarex® SV Copolyester Sheet
- Samsung Cheil Industries Starex® SF-301H Expandable Polystyrene (EPS) FR
- SABIC Innovative Plastics LNP STAT-KON FX98500 PE (Asia Pacific)
- A. Schulman PP 1930-01 Polypropylene Copolymer Polypropylene
- Tra-Con Tra-Duct 2705 Room Temperature Conductive Nickel Epoxy Adhesive
- Fainplast Compounds Hax™ HFX 500 Crosslinkable HFFR Cable Compound
- 3M Scotch-Weld™ MG100 LO Medical Grade Instant Adhesive
Copyright © lookpolymers.com All Rights Reserved