- Fiberfil® J-60/10/E8 Polypropylene Homopolymer, 10% Glass Reinforced, Chemically coupled
Fiberfil® J-60/10/E8 Polypropylene Homopolymer, 10% Glass Reinforced, Chemically coupled
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | FiberFil |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Fiberfil® J-60/10/E8 Polypropylene Homopolymer, 10% Glass Reinforced, Chemically coupled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by FIBERFIL Engineered Plastics
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.970 g/cc | 0.970 g/cc | ASTM D792 |
| Water Absorption | 0.030 % | 0.030 % | 24 hr; ASTM D570 |
| Linear Mold Shrinkage | 0.0060 cm/cm @Thickness 6.35 mm |
0.0060 in/in @Thickness 0.250 in |
ASTM D955 |
| 0.0060 cm/cm @Thickness 3.17 mm |
0.0060 in/in @Thickness 0.125 in |
ASTM D955 | |
| Melt Flow | 8.0 g/10 min | 8.0 g/10 min | 230/2.16 (typical); ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 100 - 110 | 100 - 110 | ASTM D785 |
| Tensile Strength, Yield | 58.6 MPa | 8500 psi | ASTM D638 |
| Elongation at Yield | 4.5 % | 4.5 % | ASTM D638 |
| Tensile Modulus | 3.03 GPa | 440 ksi | ASTM D638 |
| Flexural Strength | 72.4 MPa | 10500 psi | ASTM D790 |
| Flexural Modulus | 2.69 GPa | 390 ksi | Tangent; ASTM D790 |
| Izod Impact, Notched | 0.427 J/cm @Thickness 3.17 mm |
0.800 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 149 °C | 300 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 138 °C | 280 °F | ASTM D648 |
Users viewing this material also viewed the following:
- S&E Specialty Polymers GF-1831 PVC
- PolyOne Bergamid™ A70 G25 H natur TM-X Polyamide 66 (Nylon 66)
- Total Finathene® WR 201 B N HDPE blow molding (discontinued **)
- Karina E 02/127-FC-LMP Yellow Color Concentrate for PVC
- Solvay TECHNYL® A 60 G2 V30 PA66, 30% glass fiber, DRY
- SABIC Innovative Plastics PC2200R PC (Asia Pacific)
- American Elements Gold Nanoparticles
- ChevronTexaco Vistac® ISO 220 Way Oil D
- 3M Hi-Strength 94 ET Spray Adhesive-Low VOC
Copyright © lookpolymers.com All Rights Reserved